1) stepwise cracking
台阶状破裂
2) stepwise cracking
阶式破裂
3) Bench blasting
台阶爆破
1.
Structure and theory of intelligence expert system for bench blasting design;
台阶爆破设计专家系统结构与原理
2.
Simulation on effect of stemming length to deep hole bench blasting;
堵塞长度对台阶爆破作用影响的数值模拟
3.
Experimental investigation on fracture process of multi-hole bench blasting;
多孔台阶爆破破裂过程的模型试验研究
4) rupture state
破裂状态
1.
Under the hypothesis that the block moves in a straight line in every time step, the ending of analysis of the block movement is determined according to the movement law of blocks and rupture states o.
根据岩块的运动规律和结构面的破裂状态判断是否结束岩块的运动分析 ,于是判断出岩块的稳定性 。
5) granular fracture
粒状破裂
6) sidestep shape
台阶状
1.
After monitoring surface displacement of some representative landslides in Xiangxi River,the monitoring data show that Bazimen and Baijiabao landslides deformation curves are sidestep shape,and Gengjiaping s is pulsatile.
对香溪河段典型滑坡进行了长期地表位移监测,获得八字门滑坡和白家包滑坡的变形曲线为台阶状,耿家坪滑坡的变形曲线为脉动形。
补充资料：台阶状破裂
分子式：
CAS号：
性质：钢的氢致开裂的一种类型。氢原子进入钢中后聚集在沿轧制方向分布的非金属夹杂物界面处，并转变为氢分子。氢压达一定程度时就导致沿轧制方向的内裂纹。当夹杂物相互间距离较近时，由于裂纹尖端应力场的相互作用，往往产生一系列呈台阶状分布的内裂纹。主要发生在碳钢和低合金钢制的化工、石油或天然气设备与管道中。介质中的硫化氢是破裂的诱因，钢中沿轧制方向分布的硫化锰等夹杂物对破裂有促进作用。
CAS号：
性质：钢的氢致开裂的一种类型。氢原子进入钢中后聚集在沿轧制方向分布的非金属夹杂物界面处，并转变为氢分子。氢压达一定程度时就导致沿轧制方向的内裂纹。当夹杂物相互间距离较近时，由于裂纹尖端应力场的相互作用，往往产生一系列呈台阶状分布的内裂纹。主要发生在碳钢和低合金钢制的化工、石油或天然气设备与管道中。介质中的硫化氢是破裂的诱因，钢中沿轧制方向分布的硫化锰等夹杂物对破裂有促进作用。