1) sol-gel spinning
溶胶-凝胶纺丝
2) gel spinning
凝胶纺丝
1.
The fundamental principle and technological characteristics of gel spinning process were described.
论述了用超高相对分子质量柔性链聚合物制取超高强高模纤维的研究开发状况,凝胶纺丝技术的基本原理和工艺特征,所制得的具有高强度、高模量纤维的性能和应用领
2.
Ultrahigh molecular weight polyethylene fibers(UHMWPE) of different gel concentration were prepared using gel spinning process followed by solvent extraction,drying and drawing.
采用凝胶纺丝工艺制备了具有不同质量分数的超高分子质量聚乙烯凝胶纤维,并对其进行了萃取干燥和后拉伸等处理。
3) gel-spinning
凝胶纺丝
1.
Research on gel-spinning of polytetrafluoroethylene fibers
聚四氟乙烯纤维的凝胶纺丝
2.
Prepare the high-performance fibers of CNTs/PAN via gel-spinning could obtain the high fiber orientation, mechanical properties, and less fiber structural defects PAN precursor fiber.
通过能够制备高性能纤维的凝胶纺丝法将碳纳米管/聚丙烯腈纺丝原液纺丝,将碳纳米管的增强作用和凝胶纺丝法相结合,期望能够寻找一条新的制备取向度高,力学性能强,结构缺陷少的聚丙烯腈原丝的途径。
3.
The influence of the addition of NaCl and the change of NaC1 content on PVA gel-spinning is analyzed in this article.
分析NaCl的加入和NaCl含量的变化对PVA凝胶溶液的影响,并通过凝胶纺丝法制得了不同含量NaCl的PVA/NaCl纤维,对其进行表征。
4) mixed-gel spinning
凝胶纺丝
1.
Poly(vinyl alcohol)/Hydrotalcite(PVA/HT) blend fibers were prepared by mixed-gel spinning.
采用凝胶纺丝法制备聚乙烯醇/水滑石(PVA/HT)共混纤维。
2.
Biocompatible nano-hydroxyapatite/poly(vinyl alcohol)(n-HAP/PVA)blend composition fibers were prepared by mixed-gel spinning.
通过凝胶纺丝法制备具有生物相容性的纳米羟基磷灰石/聚乙烯醇(n-HAP/PVA)共混复合纤维。
5) gel spinning
[纺]凝胶纺丝
6) solvent wet-cooling gel spinning
溶剂湿法冷却凝胶纺丝
补充资料：溶胶-凝胶纺丝
分子式：
CAS号：
性质：指通过溶胶-凝胶法配制有机和无机混合聚合物凝胶并成纤的新方法。靠它可较简便地制备碳化硅和氮化硅长丝，成本低。制备过程是在四乙氧基硅烷和酚醛树脂的乙醇溶液中添加水与盐酸，调制成溶胶后加热至65℃增稠形成凝胶状，然后纺丝成纤，在1500℃氩气中烧成而得SiC纤维，若改在氨气中烧成则得Si3N4纤维。该法还可用于制备碳化硅与碳化钛混合长丝，也可以用造纸废液中的木质素代替上述酚醛树脂。
CAS号：
性质：指通过溶胶-凝胶法配制有机和无机混合聚合物凝胶并成纤的新方法。靠它可较简便地制备碳化硅和氮化硅长丝，成本低。制备过程是在四乙氧基硅烷和酚醛树脂的乙醇溶液中添加水与盐酸，调制成溶胶后加热至65℃增稠形成凝胶状，然后纺丝成纤，在1500℃氩气中烧成而得SiC纤维，若改在氨气中烧成则得Si3N4纤维。该法还可用于制备碳化硅与碳化钛混合长丝，也可以用造纸废液中的木质素代替上述酚醛树脂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。