1) dilead trioxide
三氧化二铅
2) lead sesquioxide
三氧化二铅;偏高铅酸铅
3) PbO2
二氧化铅
1.
The characterizations of Ti/SnO2+Sb2O3/PbO2 anodes with SnO2+Sb2O3 as an intermediate layer obtained by way of a polymeric precursor, and using ethylene glycol, ethanol and n-butanol for different precursor solvents were studied.
研究了以乙二醇与柠檬酸反应制得的乙二醇柠檬酸酯溶液、乙二醇、乙醇、正丁醇为前驱体溶剂制备的锡锑中间层对Ti/SnO2+Sb2O3/PbO2电极性能的影响,用XRD、ESEM对不同前驱体制备的锡锑中间层和对应的二氧化铅活性层进行了表征,并用极化曲线法和阳极寿命快速检测法比较了不同前驱体对Ti/SnO2+Sb2O3/PbO2电极的阳极寿命和在1。
2.
During electrodepositing pure lead dioxide, the electrocatalytic activity of PbO2 electrodes, as well as their stability, can often be considerably enhanced by the incorporation of some foreign ions or fine particles added to the electrodeposition solution.
二氧化铅作为阳极由于具有高的催化活性、高的析氧过电位和化学惰性而受到关注。
4) lead dioxide
二氧化铅
1.
A delamination-resistant lead dioxide electrode deposited on iron;
抗脱落铁基二氧化铅电极的研究
2.
Research on the treatment of organic dyeing wastewater by a novel lead dioxide electrode;
新型二氧化铅电极处理有机染料废水的研究
3.
The electrocatalytic activity of lead dioxide and manganese dioxide has been discussed according to the theory of molecular orbit and quantum chemistry calculation.
用恒电流法研究了PbO_2—Ti/MnO_2电极上析氧反应动力学,得到了析氧反应动力学参数,反应历程及控制步骤;用分子轨道理论和量子化学计算分析了二氧化铅电极与二氧化锰电极的电催化性能,得到了与实验结果相一致的结论。
6) lead-dioxide membrane
二氧化铅膜
补充资料：三氧化二铅
分子式：Pb2O3
CAS号：
性质：红黄色或绿棕色粉状物。不溶于冷水或氢氧化钾溶液。可被浓酸分解为二氧化铅和氧化铅。370℃左右放出氧，余留下四氧化三铅，约530℃左右时余留下氧化铅。在热水中徐徐分解。可将氧化铅溶于氢氧化钠，然后通入臭氧氧化制得。用于制取其他铅的氧化物。
CAS号：
性质：红黄色或绿棕色粉状物。不溶于冷水或氢氧化钾溶液。可被浓酸分解为二氧化铅和氧化铅。370℃左右放出氧，余留下四氧化三铅，约530℃左右时余留下氧化铅。在热水中徐徐分解。可将氧化铅溶于氢氧化钠，然后通入臭氧氧化制得。用于制取其他铅的氧化物。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条