1) pigment yellow 34
浅铬黄
2) chrome yellow
铬黄
1.
The quality of the chrome yellow product can meet the national standard of GB/T 3184 -2008.
利用净化后的含铬废水和含铅废水制备铬黄。
5) zinc chrome yellow
锌铬黄
1.
The electrochemical impedance spectroscopy (EIS) features and the resistance to corrosion of an epoxy coating containing the pigment of zinc chrome yellow have been studied with the aid of EIS and Fourier transform infrared spectroscopy (FTIR) analysis.
运用电化学阻抗谱(EIS)和Fourier变换红外光谱研究了经过不同老化温度和老化时间处理的含锌铬黄防锈颜料的环氧酯漆在3。
2.
The resistance to corrosion of an epoxy coating containing the pigment of zinc chrome yellow was studied using electrochemical impedance spectroscopy (EIS).
利用电化学阻抗谱(EIS)技术研究了含有锌铬黄防锈颜料的环氧酯漆涂层的耐蚀性能。
3.
The investigation of corrosion resistance of epoxy coating containing pigment of zinc chrome yellow was made using electrochemical impedance spectroscopy(EIS) measurement.
利用电化学阻抗 (EIS)技术研究了含有锌铬黄防锈颜料的环氧树脂涂层的耐蚀性能 。
6) lemon chrome yellow
柠檬铬黄
补充资料：浅铬黄
分子式：
CAS号：
性质：又称颜料黄34。主要成分为铬酸铅和硫酸铅固熔体的铬酸铅颜料，其化学组成为PbCrO4·xPbSO4，其中PbCrO4约为65%～71%，PbSO4约为23%～30%，随PbSO4含量增加外观为浅黄至柠檬黄色粉末，为单斜晶形或斜方晶形，密度为5.0～6.1g/cm3，吸油量为14～28g/100g，抗渗色性好，遮盖力优，亮度与中铬黄相等，优于深铬黄，碳酸性与中铬黄相等，优于深铬黄，耐碱性差，分散性较好。浅铬黄是用可溶性铅盐例如硝酸铅、铬酸盐（如重铬酸钠）和硫酸盐为原料，严格控制反应物浓度、加入速度、温度、搅拌速度、反应时间及加入的稳定剂，生成适宜晶形、粒度及其分布和稳定程度的浅铬黄粒子，经过滤、干燥和粉碎而成。主要用于工业涂料、建筑涂料、油墨和塑料。
CAS号：
性质：又称颜料黄34。主要成分为铬酸铅和硫酸铅固熔体的铬酸铅颜料，其化学组成为PbCrO4·xPbSO4，其中PbCrO4约为65%～71%，PbSO4约为23%～30%，随PbSO4含量增加外观为浅黄至柠檬黄色粉末，为单斜晶形或斜方晶形，密度为5.0～6.1g/cm3，吸油量为14～28g/100g，抗渗色性好，遮盖力优，亮度与中铬黄相等，优于深铬黄，碳酸性与中铬黄相等，优于深铬黄，耐碱性差，分散性较好。浅铬黄是用可溶性铅盐例如硝酸铅、铬酸盐（如重铬酸钠）和硫酸盐为原料，严格控制反应物浓度、加入速度、温度、搅拌速度、反应时间及加入的稳定剂，生成适宜晶形、粒度及其分布和稳定程度的浅铬黄粒子，经过滤、干燥和粉碎而成。主要用于工业涂料、建筑涂料、油墨和塑料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。