1) N,N-digly-Cidyl p-hydroxylaniline glycidyl ether
三缩水甘油基对氨基苯酚
2) the diglycidylether of 4-hydroxy-phenyl 4-hydroxy-benzoate
对羟基苯甲酸对苯二酚二缩水甘油醚
3) 2-biphenylyl glycidyl ether
邻苯基苯酚缩水甘油醚
4) Glycidyl ether of para-sec-butylphenol
对仲丁基苯酚缩水甘油醚
5) diglycidylether of 4-hydroxyphenyl-4,4'-dihydroxybenzo-ate(PHQEP)
4,4'-二对羟基苯甲酸对苯二酚二缩水甘油醚(PHQEP)
6) tribromophenyl glycidyl ether
三溴苯基缩水甘油醚
1.
The flame retardant polyether polyol phosphonate/phosphite(PEPP) was synthesized with trimethylphosphite and flame retardant polyether polyol prepared by glycerol as initiation and tribromophenyl glycidyl ether as flameretardant raw materials.
以三溴苯基缩水甘油醚为阻燃单体 ,与环氧丙烷 /环氧氯丙烷共聚制备具有阻燃特性聚醚多元醇 ,后者与亚磷酸三甲酯的酯交换反应和Arbuzov重排反应 ,合成了新型聚醚多元醇亚磷 (膦 )酸酯 (PEPP)高分子阻燃剂。
2.
The functional modification of hydroxyl-caped polyether polyurethane prepolymer(PU) with tribromophenyl glycidyl ether(TBPGE) catalyzed by n-C4H9Li and Et3N was studied.
在碱催化剂作用下,含有环氧基的阻燃剂三溴苯基缩水甘油醚(TBPGE)可以对聚醚聚氨酯进行阻燃和羟基化等功能化改性。
补充资料：三缩水甘油基对氨基苯酚
分子式：
CAS号：
性质：又称对氨基苯酚环氧树脂或三缩水甘油基对氨基苯酚。含对氨基苯酚结构的环氧树脂。红棕色液体，黏度(Pa·s)0.55～0.85，环氧值106～115，固化物拉伸强度65.7MPa，弯曲强度142.2MPa，热变形温度202℃，体积电阻率3×1016Ω·cm。由对氨基苯酚与环氧氯丙烷反应制得。主要用作玻璃布层合板，玻纤缠绕制品，用作航空航天器材，体育器材；微电机零部件的铸塑品、密封、耐高温胶黏剂等。
CAS号：
性质：又称对氨基苯酚环氧树脂或三缩水甘油基对氨基苯酚。含对氨基苯酚结构的环氧树脂。红棕色液体，黏度(Pa·s)0.55～0.85，环氧值106～115，固化物拉伸强度65.7MPa，弯曲强度142.2MPa，热变形温度202℃，体积电阻率3×1016Ω·cm。由对氨基苯酚与环氧氯丙烷反应制得。主要用作玻璃布层合板，玻纤缠绕制品，用作航空航天器材，体育器材；微电机零部件的铸塑品、密封、耐高温胶黏剂等。