1) conditions for glass formation
玻璃生成条件
2) glass former
玻璃生成体
3) glass former
玻璃生成物
4) formation condition
生成条件
1.
Measurement and calculation of hydrate formation conditions for natural gases;
天然气水合物生成条件的测定和计算
2.
The hydrate formation conditions of five gas condensates in pure water,brine and aqueous alcohol solution were measured using"pressure search"method.
利用全透明蓝宝石水合物静力学实验装置 ,采用“压力搜索法” ,分别测定了 5种凝析气的水合物生成条件 ,实验体系包括纯水、地层水以及含醇的水溶液和地层水溶液 ,共 9个体系 ,5 8个数据点。
3.
Gas hydrate equilibrium formation conditions for a synthetic natural gas in aqueous solutions containing salts and methanol were measured using ‘Pressure Search’method on the self setup gas hydrate apparatus,in the temperature range of 260 8～281 5 K and in the pressure range of 0 78～ 11 18 MPa.
１８ＭＰａ下，采用“压力搜索法”在自行设计和组建的实验装置上测定了一个合成天然气在含盐以及含盐和甲醇水溶液体系中的水合物平衡生成条件，共１１个体系７２个数据点。
5) Forming conditions
生成条件
1.
As results the projection of natural gas hydrate forming conditions mustbe taken into alcohol and salts mixing system account in practice.
本文应用基于双过程水合物生成动力学机理的Chen&Guo模型,选用PT状态方程结合基于局部组成概念的混合规则以及Debye-Huckel远程作用修正项,将水合物生成条件预测成功应用于醇盐混合体系,计算结果比较理想,从而为水合物的现场防治提供了依据。
6) glass production cost
玻璃生产成本
补充资料：玻璃生成条件
分子式：
CAS号：
性质：生成氧化物玻璃的必要条件是引入足够的玻璃生成物。玻璃生成物本身又必须满足以下条件：(1)熔体在结晶温度时有足够高的黏度，可使晶核形成和长大受阻；(2)在结晶温度时，熔体中应出现大型的、无规则的原子集团，类似于架、层(或链)，且相互交替，以致冷却时不易重新排列成长程有序的晶体；(3)玻璃生成物中的化学键应是混合键类型(离子-共价，金属-共价)；(4)作为熔体结构单元的配位多面体宜以顶角相连。以上各点仅为含有一种单纯氧化物的玻璃的生成条件。通常玻璃体为多元氧化物系统，组成复杂，但石英玻璃为单一组成，其形成原因就是因为高温下石英熔体具有足够高的黏度，冷却时不易析晶之故。
CAS号：
性质：生成氧化物玻璃的必要条件是引入足够的玻璃生成物。玻璃生成物本身又必须满足以下条件：(1)熔体在结晶温度时有足够高的黏度，可使晶核形成和长大受阻；(2)在结晶温度时，熔体中应出现大型的、无规则的原子集团，类似于架、层(或链)，且相互交替，以致冷却时不易重新排列成长程有序的晶体；(3)玻璃生成物中的化学键应是混合键类型(离子-共价，金属-共价)；(4)作为熔体结构单元的配位多面体宜以顶角相连。以上各点仅为含有一种单纯氧化物的玻璃的生成条件。通常玻璃体为多元氧化物系统，组成复杂，但石英玻璃为单一组成，其形成原因就是因为高温下石英熔体具有足够高的黏度，冷却时不易析晶之故。