2) glass fiber reinforced PA66
玻纤增强尼龙66
1.
The effects of red phosphorus flame-retardant masterbatch on the flame-retardant properties of glass fiber reinforced PA66 were investigated.
研究红磷阻燃母粒对玻纤增强尼龙66(PA66)阻燃性能的影响。
2.
In an attempt to overcome the drawbacks of direct application of red phosphorous in glass fiber reinforced PA66,the preparation technology of red phosphorous-based microcapsule fire retardant by in-situ polymerization was studied.
为克服红磷直接应用于玻纤增强尼龙66中的缺点,研究了用原位聚合法制备微胶囊红磷的工艺,测试了样品的吸湿性以及表面包覆性能,并研究了其用于玻纤增强尼龙66的阻燃性能和力学性能。
4) short glass fibre reinforced Nylon 6 (SGF-Nylon 6)
短玻璃纤维增强尼龙6
1.
The impact fracture behavior of short glass fibre reinforced Nylon 6 (SGF-Nylon 6) was studied using an instrumented izod impact approach.
用仪器化冲击实验研究短玻璃纤维增强尼龙6的无缺口冲击性能。
6) glass-fiber reinforced nylon 1010
玻璃纤维增强尼龙 1010
补充资料：玻璃纤维增强尼龙66
分子式：
CAS号：
性质：GFRPA66 以尼龙66树脂为粘接基料，玻璃纤维为增强材料，添加各种加工助剂，经熔融剪切混炼(或经熔融包覆)制得的塑料。玻纤含量一般在15％～43％之间，有众多牌号。具有增强尼龙的通性。力学强度随玻纤含量增加明显提高。30％短玻纤增强尼龙66是其代表性产品，其性能如下：相对密度1.37，熔点260℃，拉伸强度170MPa，弯曲强度240MPa，弯曲模量8000MPa，热变形温度235℃，体积电阻率1015Ω·cm，绝缘强度(干态)≥17kV/mm。适宜注塑和挤出。广泛用于汽车、机械、电器、化工等领域制造耐热耐油耐磨高强度制件如换向柱手柄、门手、汽缸盖、壳体、管、齿轮等。
CAS号：
性质：GFRPA66 以尼龙66树脂为粘接基料，玻璃纤维为增强材料，添加各种加工助剂，经熔融剪切混炼(或经熔融包覆)制得的塑料。玻纤含量一般在15％～43％之间，有众多牌号。具有增强尼龙的通性。力学强度随玻纤含量增加明显提高。30％短玻纤增强尼龙66是其代表性产品，其性能如下：相对密度1.37，熔点260℃，拉伸强度170MPa，弯曲强度240MPa，弯曲模量8000MPa，热变形温度235℃，体积电阻率1015Ω·cm，绝缘强度(干态)≥17kV/mm。适宜注塑和挤出。广泛用于汽车、机械、电器、化工等领域制造耐热耐油耐磨高强度制件如换向柱手柄、门手、汽缸盖、壳体、管、齿轮等。