1) octaethylcyclotetrasiloxane
八乙基环四硅氧烷
2) octaethylcyclotetrasilazane
八乙基环四硅氮烷
3) octamethyl cyclotetrasiloxane(D4)
八甲基环四硅氧烷(D4)
4) octamethylcyclotetrasiloxane
八甲基环四硅氧烷
1.
Study on octamethylcyclotetrasiloxane modified acrylate emulsion polymerization
八甲基环四硅氧烷改性丙烯酸酯乳液的研究
2.
Self-crosslinking silicone modified acrylate emulsion is prepared by emulsion polymerization with octamethylcyclotetrasiloxane,vinyl siloxane coupling agent and acrylate monomers as raw materials.
以八甲基环四硅氧烷(D4)、乙烯基硅烷偶联剂和丙烯酸单体为原料,采用乳液聚合工艺制得自交联型硅丙乳液,研究了有机硅单体及硅烷偶联剂用量对乳液性能的影响。
3.
Densities,surface tensions and viscosities for binary mixtures of xylene with octamethylcyclotetrasiloxane(D4),include D4+o-xylene,+m-xylene and+p-xylene systems,were measured over the whole composition range at 298.
测定了八甲基环四硅氧烷(D4)分别与邻二甲苯、间二甲苯和对二甲苯组成的二元混合物在298。
5) octamethyl cyclotetrasiloxane
八甲基环四硅氧烷
1.
The polysiloxane emulsion of octamethyl cyclotetrasiloxane and tetravinyl tetramethyl cyclotetrasiloxane was prepared using sodium dodecyl benzene sulfonate as an emulsifier and sulfuric acid as catalyst.
以十二烷基苯磺酸钠(SDBS)为乳化剂、硫酸为催化剂,将八甲基环四硅氧烷(D4)与四甲基四乙烯基环四硅氧烷(D4Vi)进行正离子开环共聚,制备了聚硅氧烷乳液。
6) octaphenylcyclotetrasiloxane
八苯基环四硅氧烷
1.
Study on Synthesis of octaphenylcyclotetrasiloxane;
八苯基环四硅氧烷的合成研究
补充资料：八乙基环四硅氧烷
分子式：[(C2H5)2SiO]4
CAS号：
性质：沸点127℃（133Pa）。溶点-64℃。相对密度0.964。折射率1.4336。在微量的硅醇钠、硅醇钾或少量浓硫酸作用下，分子内Si—O—Si键断裂重排，生成直链的聚硅氧烷和环状硅氧烷的混合物。这种催化断裂重排过程具有平衡特性，在环体开环聚合成高分子量聚合物时，也发生大分子断裂降解。与过量的氢氧化钠甲醇溶液反应，生成二乙基硅二醇钠。可由二乙基二氯硅烷的水解料与KOH进行高温裂解来制取。用来制备耐低温的乙基硅油和乙基硅橡胶。
CAS号：
性质：沸点127℃（133Pa）。溶点-64℃。相对密度0.964。折射率1.4336。在微量的硅醇钠、硅醇钾或少量浓硫酸作用下，分子内Si—O—Si键断裂重排，生成直链的聚硅氧烷和环状硅氧烷的混合物。这种催化断裂重排过程具有平衡特性，在环体开环聚合成高分子量聚合物时，也发生大分子断裂降解。与过量的氢氧化钠甲醇溶液反应，生成二乙基硅二醇钠。可由二乙基二氯硅烷的水解料与KOH进行高温裂解来制取。用来制备耐低温的乙基硅油和乙基硅橡胶。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。