1) LTV silicone gum
低温硫化硅橡胶
2) room-temperature vulcanized silicone rubber
室温硫化硅橡胶
1.
Enhancing methods of room-temperature vulcanized silicone rubber adhesive;
室温硫化硅橡胶胶粘剂的增强方法
2.
With PDMS(polydimethyl siloxane)of appropriate viscosity as matrix and addition of appropriate fillers and assistants,the room-temperature vulcanized silicone rubber coatings was successfully prepared.
采用一定粘度的聚二甲基硅氧烷为基体,加入适量填料和助剂,成功制备了室温硫化硅橡胶涂层。
3.
With hydroxyl group terminated PDMS on both side as feedstock, adding several kinds of fillers and adjuvants, the room-temperature vulcanized silicone rubber coatings are prepared.
以二羟基聚二甲基硅氧烷(PDMS)为基体,加入不同填料和助剂,制备了室温硫化硅橡胶涂层。
3) room temperature vulcanized silicone rubber
室温硫化硅橡胶
1.
Modified room temperature vulcanized silicone rubber adhesive filled in situ with silica white;
白炭黑原位填充的改性室温硫化硅橡胶胶黏剂
2.
Research progress in thermal conductive room temperature vulcanized silicone rubber;
导热室温硫化硅橡胶的研究进展
3.
Progress in reinforcemnet and modification of room temperature vulcanized silicone rubber;
室温硫化硅橡胶的增强改性研究进展
4) RTV silicone rubber
室温硫化硅橡胶
1.
Modification of RTV silicone rubber by nano-SiOx;
纳米SiOx改性室温硫化硅橡胶研究
2.
The structure and the surface characteristics of fumed silica and its application in HTV silicone rubber and RTV silicone rubber were introduced as well.
简述了气相法白炭黑的发展及国内生产情况 ,介绍了气相法白炭黑的结构和表面性质 ,以及在热硫化硅橡胶和室温硫化硅橡胶中的应用。
3.
The features and application of the operating agent for adjusting the rate of extrusion and the thixotropy of the compound, the thinner for improving the fluidity of the compound, and the plasticizer for regulating the hardness and the modulus of vulcanized compound used in RTV silicone rubber of condensed type were described.
介绍了缩合型室温硫化硅橡胶中常用的调节胶料挤出速度及触变性的施工助剂、改善胶料流动性的稀释剂、调节胶料硫化后硬度及模量的增塑剂的特点和作用。
5) HTV rubber
高温硫化硅橡胶
1.
It is considered that degradation of hydrophobicity,mechanical strength and pollution deposit which effect their long term service reliability,is caused by HTV rubber ageing.
对大量运行的高温硫化硅橡胶(HTV)绝缘子进行了憎水性试验、低温模拟试验、灰密对憎水性的影响以及耐漏电起痕及电蚀损试验,认为高温硫化硅橡胶因老化而引起的憎水性下降、机械强度下降及积污性能下降影响其长期工作的可靠性,所以评价复合硅橡胶的憎水性能除憎水性分级HC值外,还应重点突出评价憎水性的减弱(丧失)特性、憎水性的恢复特性及憎水性的迁移特性。
6) cold rubber
低温硫化橡胶
补充资料：低温硫化硅橡胶
分子式：
CAS号：
性质：由乙烯基封端的二甲基聚硅氧烷和甲基含氢硅油两个组分组成，在铂催化剂存在下，可硫化成透明弹性体。添加增强树脂的低温硫化硅橡胶，硫化后的制品的硬度(邵氏A)≥40、拉伸强度≥4.41MPa、相对伸长率≥70％。可由乙烯基封端的二甲基聚硅氧烷和甲基含氢硅油，按一定比例混合，在铂催化剂存在下，于70～80℃加热硫化来制取。用于各种电子元件的密封、固体电路和微膜组件的包封、飞机和汽车风挡的夹层材料和人造角膜等。
CAS号：
性质：由乙烯基封端的二甲基聚硅氧烷和甲基含氢硅油两个组分组成，在铂催化剂存在下，可硫化成透明弹性体。添加增强树脂的低温硫化硅橡胶，硫化后的制品的硬度(邵氏A)≥40、拉伸强度≥4.41MPa、相对伸长率≥70％。可由乙烯基封端的二甲基聚硅氧烷和甲基含氢硅油，按一定比例混合，在铂催化剂存在下，于70～80℃加热硫化来制取。用于各种电子元件的密封、固体电路和微膜组件的包封、飞机和汽车风挡的夹层材料和人造角膜等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条