1) low alkali ceramics
低碱陶瓷
2) alkali free ceramics
无碱陶瓷
3) low temperature ceramic
低温陶瓷
1.
A kind of super-low temperature ceramic was obtained by investigating the sintering kinetics of prescription consisted of waste glass powders and sintering aluminum oxide etc.
通过对由玻璃粉料与熟矾土等结晶态原料组成的配方的烧结动力学研究,获得了一种性能与传统长石瓷相当而烧成温度仅860℃左右的超低温陶瓷,并对“准非反应”烧结机理进行了初步探讨。
2.
This paPer systematicall}' summarized the current status of the studyof low temperature ceramics, main production technologies and application.
本文对低温陶瓷研究的现状、主要生产技术及其应用作了较系统的综述，以废玻璃、熟矾土、粘土为主要原料，研制了一种烧结温度范围在850-870℃之间的低温陶瓷，用X射线衍射仪测定了材料的物相组成，其主晶相为刚玉；用扫描电子显微镜观察了材料的显微结构。
5) low dielectric constant ceramic
低介电陶瓷
6) LTCC
低温共烧陶瓷
1.
Researches and Development of Borosilicate Glass in LTCC Technology;
低温共烧陶瓷用硼硅酸盐玻璃的研究进展
2.
Current Status and Developmental Trend of LTCC;
低温共烧陶瓷的现状和发展趋势
3.
Soldering of SiC particulate reinforced aluminum(Al/SiC) and low temperature co fired ceramic (LTCC) materials;
铝基碳化硅增强材料(Al/SiC)和低温共烧陶瓷(LTCC)的钎焊
补充资料：低碱陶瓷
分子式：
CAS号：
性质：主晶相为莫来石(3Al2O3·2SiO2)，并含少量钙长石(CaO·Al2O3·2SiO2)、钡长石(BaO·Al2O3·2SiO2)晶相所组成的陶瓷材料。其特点原料来源充足，成本低。瓷体含氧化钾、氧化钠量较少(R2O≤1.2％)，在直流负荷下老化后电阻值变化较小。相对介电常数≤8[1MC,(20±5)℃)。击穿强度大于8kV/mm。体积电阻率大于10Ω·cm。抗折强度大于78MPa。主要原料为高岭土、石英、方解石，碳酸钡等，可用一般陶瓷工艺制造。可用于制作高温和高稳定性碳素膜、金属膜、沉积膜电阻器基体。
CAS号：
性质：主晶相为莫来石(3Al2O3·2SiO2)，并含少量钙长石(CaO·Al2O3·2SiO2)、钡长石(BaO·Al2O3·2SiO2)晶相所组成的陶瓷材料。其特点原料来源充足，成本低。瓷体含氧化钾、氧化钠量较少(R2O≤1.2％)，在直流负荷下老化后电阻值变化较小。相对介电常数≤8[1MC,(20±5)℃)。击穿强度大于8kV/mm。体积电阻率大于10Ω·cm。抗折强度大于78MPa。主要原料为高岭土、石英、方解石，碳酸钡等，可用一般陶瓷工艺制造。可用于制作高温和高稳定性碳素膜、金属膜、沉积膜电阻器基体。