1) drawing force
抽出力
2) H pull-out
H抽出力
1.
The results showed that the t_(10)and t_(90)of rubber compound extended a little by using superfine active kaolin partly instead of carbon black in inner ply and outer ply compounds,and the physical properties of vulcanizate and H pull-out after aging changed little;the endu-rance of finished tire improved and the cost of rubber compound reduced.
结果表明,在内层和外层帘布胶中以超细活性高岭土部分替代炭黑后,胶料的t10和t90稍有延长,硫化胶的物理性能及老化后H抽出力基本相当;成品轮胎耐久性能提高,胶料成本降低。
2.
The results showed that the scorch time extended,the curing speed reduced,the anti-reversion improved,and the better tensile,elongation and tear properties were obtained using TBSI instead of TBBS by equal weight in the upper bead filler compound;and the scorch time extended,t_(90) reduced,the permanent tensile set decreased and the H pull-out changed little using 1 phr of TBSI instead of 1.
在胎体胶配方中以 1份促进剂TBSI替代 1 2 5份促进剂DZ ,胶料的焦烧时间延长 ,t90 缩短 ,硫化胶的拉断永久变形减小 ,H抽出力相当。
3) H pull-out force
H抽出力
1.
The results showed that when compared to the dry cobalt decanoate,the wet cobalt decanoate gave NR vulcanizate higher H pull-out force,lower H pull-out force loss after hot air aging and brine aging and similar physical properties.
结果表明,与干法工艺生产的癸酸钴相比,采用湿法工艺生产的癸酸钴可提高NR硫化胶的H抽出力,经热空气老化和盐水老化后硫化胶的H抽出力下降率较小,其它物理性能基本相当。
4) fiber withdrawal force
纤维抽出力
6) extraction
[英][ɪk'strækʃn] [美][ɪk'strækʃən]
抽出
1.
The harms and principles of the migration and extraction of plasticizer from the PVC were discussed.
讨论了聚氯乙烯(PVC)中增塑剂抽出和迁移的危害性和基本原理,重点介绍了影响增塑剂抽出和迁移的主要因素,如:增塑剂相对分子质量和分子结构、环境温度、增塑剂含量、介质和时间。
补充资料：抽出力
分子式：
CAS号：
性质：将帘线两端按规定长度埋在胶条中，硫化后测定单根帘线沿轴向从胶条中抽出时所需的力。所测性能是作用于帘线与橡胶界面上的剪切力，它是衡量橡胶用帘线与橡胶静态黏合好坏的重要指标。帘线抽出力可以用帘线H试验进行测定。
CAS号：
性质：将帘线两端按规定长度埋在胶条中，硫化后测定单根帘线沿轴向从胶条中抽出时所需的力。所测性能是作用于帘线与橡胶界面上的剪切力，它是衡量橡胶用帘线与橡胶静态黏合好坏的重要指标。帘线抽出力可以用帘线H试验进行测定。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。