1) porous carbon whisker
多孔碳晶须
2) carbon whisker
碳晶须
3) CaCO3 whisker
碳酸钙晶须
1.
In this paper,the change of filled paper property is studied with aragonite CaCO3 whisker.
文章采用自制文石型碳酸钙晶须替代传统方解石型碳酸钙,研究其填充纸张性能的变化,结果表明:同样条件下,文石型碳酸钙晶须较传统方解石型碳酸钙填料有更高的留着率,更小的纸张强度降低率。
4) silicon carbide whisker
碳化硅晶须
1.
The key process parameters for the double-heating synthesis of silicon carbide whiskers with carbon black and SiO2 powders as raw materials are studied.
双重加热法是低成本、大批量合成碳化硅晶须的新技术,合成温度低、合成时间短、生成率高。
2.
The heat conductive silicone rubber with vinyl endblocked polymethylsiloxane as basic gum and silicone nitride(Si_3N_4) of different particle sizes and silicon carbide whisker as fillers was prepared.
以甲基乙烯基硅橡胶为基胶,选用不同粒径氮化硅粒子和碳化硅晶须为填料制备了导热硅橡胶。
3.
The silicon carbide whiskers and platelets are ideal reinforcements of compound materials of ceramic,metal and resin.
碳化硅晶须和晶片都是陶瓷基、金属基、树脂基复合材料的理想增强体,与碳化硅晶须相比,有关碳化硅晶片制备与应用的报道相对较少。
5) titanium carbide whiskers
碳化钛晶须
6) silicon carbide whiskers
碳化硅晶须
1.
All kinds of approach and the mechanism to synthesize silicon carbide whiskers are commented on , and the progress of silicon carbide whiskers at home and abroad is also reviewed.
比较详细地介绍了当前国内外碳化硅晶须的生长机理与制备方法，简要评述了对碳化 硅晶须研究的进展状况。
2.
Carbon nanotubes (CNTs) and silicon carbide whiskers (SiCw) are promising reinforcement materials for manufacturing metal or ceramic based composites.
在制备复合材料中,碳纳米管和碳化硅晶须易受到空气和基体材料侵蚀而失效。
补充资料：多孔碳晶须
分子式：
CAS号：
性质：具有多微孔表面的碳晶须。比表面积20.6m2/R，比表面积比2.1～17.8，弯曲强度和模量各为155～208MPa和5.7～6.3GPa。对树脂等基体具有良好的黏合性。制法是将直径0.8μm，平面形状比46，相对密度1.96和比表面积2.58m2/g的气相成长碳晶须，边加热至1000℃边与水蒸气和氮混合气接触而得。用于作塑料、陶瓷、金属和橡胶基复合材料增强剂及层间化合物的晶核等。
CAS号：
性质：具有多微孔表面的碳晶须。比表面积20.6m2/R，比表面积比2.1～17.8，弯曲强度和模量各为155～208MPa和5.7～6.3GPa。对树脂等基体具有良好的黏合性。制法是将直径0.8μm，平面形状比46，相对密度1.96和比表面积2.58m2/g的气相成长碳晶须，边加热至1000℃边与水蒸气和氮混合气接触而得。用于作塑料、陶瓷、金属和橡胶基复合材料增强剂及层间化合物的晶核等。