1) inverse spinel type structure
反尖晶石型结构
2) inverse spinel structure
反尖晶石结构
3) Spinel structure
尖晶石型结构
1.
The results showed that both materials doped with Cr3+ and F-and coated with Al2O3 had a spinel structure.
结果表明:LiMn2O4在掺杂Cr3+和F-及表面包覆氧化铝后仍为尖晶石型结构,随掺杂和包覆量的增加,材料首次放电容量降低,但循环性能明显改善,其中未掺杂、掺杂量为0。
4) spinel-type structure
类尖晶石型结构
5) spinel structure
尖晶石结构
1.
Effect of lithium and cobalt doping on the Li-Mn spinel structure and performance;
锂和钴元素掺杂对锂锰尖晶石结构和性能的影响
2.
Based on the practical application,the velocity and limitation of Co2+ entry into the spinel structure were studied under the condition of Co/Fe ratio in initial solution.
从实际应用的角度出发,研究了初始溶液中钴铁摩尔比对室温下Co2+进入尖晶石结构的速率和程度的影响,过程中的氧化-还原电位和产物的化学分析、XRD以及IR等光谱分析的结果表明:初始溶液中较小的钴铁摩尔比有利于钴铁酸盐的生成。
3.
The cation distribution in Zn(Ga,Fe)_2O_4 solid solutions with spinel structure were calcu- lated by using the X-ray powder diffraction density method (R factor Method).
应用X射线衍射密度法(R因子法)计算了Zn(Ga,Fe)_2O_4固溶体尖晶石结构中阳离子分布,结果表明:金属离子在ZnGa_2O_4尖晶石结构中采取中间偏反型分布。
补充资料：反尖晶石型结构
分子式：
CAS号：
性质：与尖晶石结构类同，但A，B离子所处的位置和配位关系完全相反，故名。这类结构中O2-离子与尖晶石结构中情况相同，呈立方紧密堆积，A2+离子和半数B3+离子处于八面体空隙中，而余下的一半B3+离子处于四面体空隙中。整个结构可写作，式中IV和VI为配位数。常见的反尖晶石化合物有：Fe3+，(Fe2+，Fe3+)O4，(即Fe3O4)、Fe(MgFe)O4，Zn(SnZn)O4、Fe(NiFe)O4等，这些晶体具有铁氧体磁性，在电子陶瓷中有广泛应用。
CAS号：
性质：与尖晶石结构类同，但A，B离子所处的位置和配位关系完全相反，故名。这类结构中O2-离子与尖晶石结构中情况相同，呈立方紧密堆积，A2+离子和半数B3+离子处于八面体空隙中，而余下的一半B3+离子处于四面体空隙中。整个结构可写作，式中IV和VI为配位数。常见的反尖晶石化合物有：Fe3+，(Fe2+，Fe3+)O4，(即Fe3O4)、Fe(MgFe)O4，Zn(SnZn)O4、Fe(NiFe)O4等，这些晶体具有铁氧体磁性，在电子陶瓷中有广泛应用。