1) novoloid-based activated carbon fiber
酚醛基活性碳纤维
2) novoloid-based carbon fiber
酚醛基碳纤维
3) Phenolic resin based activated carbon fiber
酚醛基活性炭纤维
1.
Phenolic resin based activated carbon fibers (ACF-H2O) prepared using steam activation at 800 ℃ were investigated by means of N2 adsorption, AC impedance and constant current discharge techniques.
利用水蒸汽活化法制备了酚醛基活性炭纤维(ACF-H2O),对其比表面积、孔结构与在LiClO4/PC(聚碳酸丙烯酯)有机电解液中的电容性能之间的关系进行了探讨。
4) phenolic resin based carbon fibers
酚醛基炭纤维
5) activated carbon fibers
活性碳纤维
1.
Design and control on the structure and function of activated carbon fibers;
活性碳纤维结构设计及功能控制
2.
Design of activated carbon fibers/epoxy resin composites;
活性碳纤维/树脂复合吸波材料的设计
6) active carbon fiber
活性碳纤维
1.
Formaldehyde adsorption and degradation was conducted in the presence of TiO2/ACF(active carbon fiber) photocatalyst prepared from TiO2 sol and ACF.
采用TiO2溶胶和活性碳纤维(ACF)制备的TiO2／ACF光催化剂吸附-降解空气中微量的甲醛。
2.
The main performance of active carbon fiber and TiO_2 composites were introduced and the application and the latest development were summarized.
简要介绍了用于空气净化的活性碳纤维负载二氧化钛复合材料的发展概况、基本性能、应用及其吸附性能研究的意义,并对活性碳纤维负载二氧化钛的主要研究思路作了简要的阐述。
3.
The removing effects of CS 2 with 6# carbon fiber,1# copper fiber,active carbon fiber and AF material are good.
不同滤料对CS2 的消除效果亦不相同 ,其中 6号碳纤维、 1号铜纤维、活性碳纤维及AF材料对CS2 的消除效果较好。
补充资料：酚醛基活性碳纤维
分子式：
CAS号：
性质：酚醛碳纤维经活化而得的活性碳纤维。直径9～11μm。比表面积1500～2500m2/g。外表面积1.0～1.2m2/g。微孔径1.5～3.5nm。强度294～392MPa。模量9.8～14.7GPa。苯吸收率30％～80％。甲基蓝吸附性310～380ml/R。制法将酚醛纤维在惰性气体保护下于900℃通入含氧水蒸气或CO2而得。用途有溶剂回收、有害气体吸附、除臭、卫生材料、空气净化、创伤绷带、电极材料、隔膜分离器、电敏元件防护罩、特殊防护服等。
CAS号：
性质：酚醛碳纤维经活化而得的活性碳纤维。直径9～11μm。比表面积1500～2500m2/g。外表面积1.0～1.2m2/g。微孔径1.5～3.5nm。强度294～392MPa。模量9.8～14.7GPa。苯吸收率30％～80％。甲基蓝吸附性310～380ml/R。制法将酚醛纤维在惰性气体保护下于900℃通入含氧水蒸气或CO2而得。用途有溶剂回收、有害气体吸附、除臭、卫生材料、空气净化、创伤绷带、电极材料、隔膜分离器、电敏元件防护罩、特殊防护服等。