1) high speed tool steel
高工钢
2) high carbon tool steels
高碳工具钢
1.
The results show that the slurry of high carbon tool steels prepared after stirring during solidification can make products without segregation and defect like network carbide which tend to occur during direct rolling.
探讨了高碳工具钢常规的加工方法和半固态流变轧制技术,结果表明将在凝固过程中进行搅拌后制备的高碳工具钢半固态浆料直接进行流变轧制,可生产出成分均匀、没有偏析的产品,消除了在常规轧制中很难克服的网状碳化物等缺陷;半固态固相颗粒细小而且星球状可生产出高强、高韧性的工具钢。
3) HSS
高速工具钢
1.
Research on Wear Failure Mechanism of HSS Nickel-coated Against Abrasive Belt Backing
渗镍高速工具钢/砂带基材的摩擦磨损实验研究
2.
The HSS samples were implanted with 3×10`17cm-2 of 60keV C ions and (2-6) 10`17cm-2 of 102keV Co ions respectively, from a MEVVA ion source.
采用ＭＥＶＶＡ源离子注入机对高速工具钢（ＨＳＳ）进行了Ｃ、 Ｃｏ及Ｃ＋Ｃｏ双注入，并做了 硬度、摩擦系数测量和磨损实验。
5) high speed steel
高速工具钢
1.
The phases presented in the microstructure of W6Mo5Cr4V2, W10Mo4Cr4V3Al and Mo5Cr4V high speed steels at the quench-heated state and the anneal - heated state have been analyaed differently, and the necessary information concerning the phase constituents in the steels at the states mention above and their variation has been obtained.
对W6Mo5Cr4V2、W10Mo4Cr4V3Al和Mo5Cr4V3种高速工具钢在淬火加热态和退火加热态的组织进行了相分析。
6) high Cr tool steel
高铬工具钢
补充资料：高工钢
分子式：
CAS号：
性质：又称高速钢，高工钢。主要用作机床高速切削刀具的高碳高合金莱氏体钢。钢中主要合金元素有W，Mo，Cr和V等。高速钢经热处理后的使用硬度可达HRC63以上，而且在600℃左右的工作温度下仍能保持较高硬度。钢的韧性、耐磨性和耐热性等均较好，退火状态的高速钢可用一般的机械切削方法加工成各种形状复杂的精密工具。高速钢按用途可分为通用高速钢和特种高速钢两大类，按其所含合金元素可分为W系Mo系和W-Mo系三大类，在每类中又有普碳和高碳、无钴与含钴以及低钒与高钒之分。高速钢用途较广，除用作切削工具之外，还常用作性能要求高的模具、轧辊和机械零件等。
CAS号：
性质：又称高速钢，高工钢。主要用作机床高速切削刀具的高碳高合金莱氏体钢。钢中主要合金元素有W，Mo，Cr和V等。高速钢经热处理后的使用硬度可达HRC63以上，而且在600℃左右的工作温度下仍能保持较高硬度。钢的韧性、耐磨性和耐热性等均较好，退火状态的高速钢可用一般的机械切削方法加工成各种形状复杂的精密工具。高速钢按用途可分为通用高速钢和特种高速钢两大类，按其所含合金元素可分为W系Mo系和W-Mo系三大类，在每类中又有普碳和高碳、无钴与含钴以及低钒与高钒之分。高速钢用途较广，除用作切削工具之外，还常用作性能要求高的模具、轧辊和机械零件等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。