1) high boron-low carbon super alloy
高硼低碳高温合金
2) low carbon high alloy steel
低碳高合金钢
1.
Influence of substituting nickel with manganese on the structure and property of the low carbon high alloy steel;
以Mn代Ni对低碳高合金钢组织性能的影响
2.
Comparison of corrosive impact abrasion behavior between low carbon high alloy steel and high manganese steel;
低碳高合金钢和高锰钢冲击腐蚀磨损特性研究
3.
Influence of impact power on impact-corrosion resistance of low carbon high alloy steel;
冲击功对低碳高合金钢冲击腐蚀磨损性能的影响
3) wire of hi-carbon and low alloy
高碳低合金钢丝
1.
In order to solve the problem of crack deformation tendency of the quenched steel wires for a uniform structure,development is done to the special wire of hi-carbon and low alloy,finding that there is variation of spheroidizing annealing processed structure under the same spheroidizing annealing process once drawed.
为了改善针布齿条淬火时的变形开裂倾向性,使其最终性能均匀,研究了针布齿条专用高碳低合金钢丝经过不同程度拉拔变形后,在相同球化退火工艺下具有差异的球化退火组织,并且比较了经较大拉拔变形后钢丝退火前后的组织差异,以及该钢丝经轧制前后的组织变化情况。
4) CrNiMo low carbon high alloy steel
CrNiMo低碳高合金钢
1.
By the EDS, X-ray diffraction and metallographic analysis, it was found that the finalmicrostructure of the CrNiMo low carbon high alloy steel is martensite after heattreatment.
借助能谱分析，X射线衍射鉴定以及金相观察，发现CrNiMo低碳高合金钢经过适当热处理后组织为单相马氏体，测定其力学性能，数据显示材料的综合性能良好，硬度和韧性搭配适宜。
5) high carbon low allyed steel
高碳低合金钢
补充资料：高硼低碳高温合金
分子式：
CAS号：
性质：一种镍基铸造高温合金。硼含量为0.05％～0.2％，碳含量小于0.05％，不同于普通铸造镍基合金的硼为0.005％～0.03％和碳为0.1％～0.25％。高硼低碳高温合金在保持普通镍基铸造高温合金高温强度的同时，中温性能特别是塑性显著提高，如Mar-M200合金在980℃时具有很高的持久强度、蠕变强度和良好的塑性，但760℃的持久塑性几乎为零，而其改型的高硼低碳B-1950合金在保持Mar-M200合金980℃优越性能的同时，760℃的持久塑性可达2％～5％。主要用于制做发动机涡轮叶片和整体铸造涡轮转子。
CAS号：
性质：一种镍基铸造高温合金。硼含量为0.05％～0.2％，碳含量小于0.05％，不同于普通铸造镍基合金的硼为0.005％～0.03％和碳为0.1％～0.25％。高硼低碳高温合金在保持普通镍基铸造高温合金高温强度的同时，中温性能特别是塑性显著提高，如Mar-M200合金在980℃时具有很高的持久强度、蠕变强度和良好的塑性，但760℃的持久塑性几乎为零，而其改型的高硼低碳B-1950合金在保持Mar-M200合金980℃优越性能的同时，760℃的持久塑性可达2％～5％。主要用于制做发动机涡轮叶片和整体铸造涡轮转子。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条