1.
Synthesis of Nanocrystalline La_(1-x)Sr_xCrO_3 by Sol-Gel Method;
溶胶-凝胶法合成纳米铬酸锶镧的工艺研究
2.
Preparation and Sintering Behavior of Nano-scale La_(1-x)Sr_xCrO_3 Powder;
纳米铬酸锶镧制备及烧结行为
3.
Nano-La_(1-x)Sr_xCrO_3 was prepared by sol-gel process and was compacted into green bodies under high pressure.
通过溶胶-凝胶法制备了铬酸锶镧(La_(1-x)Sr_xCrO_3)纳米粉体，采用高压成型、无压烧结工艺进行了烧结试验并检测了烧结体的物理性能。
5) strontium titanate ceramics
钛酸锶陶瓷
1.
Some research development on the sintering of strontium titanate ceramics was reviewed,and two major factors that affect the sintering technology and aids were summarized.
钛酸锶陶瓷电容具有高储能、低损耗、高稳定性等优点,但烧结温度高,烧成密度低。
6) strontium zirconate ceramics
锆酸锶陶瓷
补充资料：铬酸锶镧陶瓷
分子式：
CAS号：
性质： 以铬酸锶镧[(La、Sr)CrO3]为主要成分的陶瓷。其中较重要的一种为La0.84Sr0.16CrO3。制品导电性能优良，具有电子导电特性。电阻系数常温时为1Ω·cm。与铬酸镧(LaCrO3)相比，用锶取代了部分镧可改善结构性能，提高硬度、使用温度和热震性。对钾的抗蚀性也好，且能有效地降低电阻和高温挥发性。先将主要原料三氧化二镧、碳酸锶、氧化铬在高于1400℃下煅烧，合成固溶体后按常规陶瓷工艺制得。烧成温度1550℃。主要用于制作高温电热元件、磁流体发电装置的电极和代铂材料等。但长期用于1400℃以上的场合，挥发性随使用温度的增高而增大，限制了它的使用范围。
CAS号：
性质： 以铬酸锶镧[(La、Sr)CrO3]为主要成分的陶瓷。其中较重要的一种为La0.84Sr0.16CrO3。制品导电性能优良，具有电子导电特性。电阻系数常温时为1Ω·cm。与铬酸镧(LaCrO3)相比，用锶取代了部分镧可改善结构性能，提高硬度、使用温度和热震性。对钾的抗蚀性也好，且能有效地降低电阻和高温挥发性。先将主要原料三氧化二镧、碳酸锶、氧化铬在高于1400℃下煅烧，合成固溶体后按常规陶瓷工艺制得。烧成温度1550℃。主要用于制作高温电热元件、磁流体发电装置的电极和代铂材料等。但长期用于1400℃以上的场合，挥发性随使用温度的增高而增大，限制了它的使用范围。