1) extrusion-swell drying
挤压膨胀干燥
2) extruded expansion dehumidifier
挤压脱水膨胀干燥机
3) expansion drying
膨胀干燥
4) expansion dryer
膨胀干燥机
1.
Cause analysis and countermeasure for breakage of the expansion dryer mainshaft;
膨胀干燥机主轴断裂原因分析及对策
2.
Technological innovation and application of expansion dryer;
膨胀干燥机的技术改造与应用
5) expansion drying machine
膨胀干燥机
1.
The reason of breakage was found out through analysis of the breakage face on the principal axis of expansion drying machine.
通过对膨胀干燥机主轴断裂面的分析,确定了断裂是由于热处理过程中淬火处理所引起的组织变化 及组织膨胀造成的心部裂纹所致;提出了改变主轴断裂面的结构尺寸、改善主轴热处理工艺,确保淬火质量等对策。
6) expansion drying process
膨胀干燥过程
1.
The expansion drying process is the important content of the disposal technology after synthesizing rubber, it has very large windage between the calculation result and the actual situation of some research theories about the expansion drying process at present.
膨胀干燥过程是合成橡胶后处理工艺的重要组成部分,目前对膨胀干燥过程进行研究的部分理论的计算结果与实际情况存在很大的偏差。
补充资料：挤压膨胀干燥
分子式：
CAS号：
性质： 在合成橡胶后处理工艺中，为了将经脱水工序后还含有5％～15％水分的橡胶胶粒进一步干燥，以使其含水量达到要求的指标，一般常采用挤压膨胀干燥技术进行干燥。胶粒是通过膨胀干燥机实现这一过程的。胶粒进入膨胀干燥机后一面受螺杆推动沿机身向机头方向前进，一面受膨胀干燥机身夹套的蒸汽加热，同时受机中螺杆及机身挤压摩擦生热，使胶温不断上升，由于膨胀干燥机机头模板开孔面积远较机身断面为小，因此受挤压的胶料压力不断上升，至机头处温度已上升到160～170℃，压力达到4.5～5.0MPa。在此条件下，胶中所含水分仍呈液相存在。当胶料行至机头处，从模板小孔被挤出时，胶粒压力骤然下降至常压，胶中所含水分即发生闪蒸膨胀，大部分水分将被蒸发，胶粒变成松散长条，其含水量被降至0.5％，被机头外的切刀切成颗粒，温度降至800℃左右，从而完成干燥过程。
CAS号：
性质： 在合成橡胶后处理工艺中，为了将经脱水工序后还含有5％～15％水分的橡胶胶粒进一步干燥，以使其含水量达到要求的指标，一般常采用挤压膨胀干燥技术进行干燥。胶粒是通过膨胀干燥机实现这一过程的。胶粒进入膨胀干燥机后一面受螺杆推动沿机身向机头方向前进，一面受膨胀干燥机身夹套的蒸汽加热，同时受机中螺杆及机身挤压摩擦生热，使胶温不断上升，由于膨胀干燥机机头模板开孔面积远较机身断面为小，因此受挤压的胶料压力不断上升，至机头处温度已上升到160～170℃，压力达到4.5～5.0MPa。在此条件下，胶中所含水分仍呈液相存在。当胶料行至机头处，从模板小孔被挤出时，胶粒压力骤然下降至常压，胶中所含水分即发生闪蒸膨胀，大部分水分将被蒸发，胶粒变成松散长条，其含水量被降至0.5％，被机头外的切刀切成颗粒，温度降至800℃左右，从而完成干燥过程。