1) accelerated ozone ageing
加速臭氧老化
2) ozone cracking test
加速臭氧老化试验
3) ozone aging
臭氧老化
1.
The heat oxygen aging property and ozone aging property of clay/SBR and clay/NR nano-composites were studied,and the thermogravimetry and air isolation of clay/SBR nano-composite were also investigated.
研究粘土 /SBR及粘土 /NR纳米复合材料的耐热氧老化和耐臭氧老化性能 ,并考察粘土 /SBR纳米复合材料的热失重和气体阻隔性。
2.
Two adjustable CR vulcanizates to ozone aging at different conditions have been studied and results have shown tnat ozone concentration, force and deformation etc have clear effect on ozone aging Ozone aging at compression can also makc the vulcanizates produce crack and Thiol adjustable CR vulcanizate resistance to ozone aging is much better than sulfur adjustable CR vulcanizte.
通过对两种调节型的氯丁硫化胶在不同条件下的臭氧老化研究表明：臭氧浓度、受力状态、变形程度等对臭氧老化结果有明显的影响：压缩状态下的臭氧老化同样产生龟裂，硫醇调节型氯丁硫化胶抗臭氧老化性优于硫黄调节型氯丁硫化胶。
3.
The investigation of the ozone aging of SIR have been carried out under 3 different concentration of ozone(30ppm、300ppm、800ppm) with 3 varied relative humidity (25%、55%、85%).
本文设计了臭氧老化试验装置及相应的测量系统,开展了不同臭氧浓度(分别为30ppm、300ppm、800ppm)、不同相对湿度(分别为25%、55%、85%)作用下硅橡胶材料臭氧作用的试验研究,并对臭氧作用后的试样进行了扫描电镜分析、红外光谱分析、憎水性测试和热刺激电流测试等评估测试。
5) ozonization
臭氧化;加臭氧
6) Accelerated aging
加速老化
1.
General Aging Theory and Method for Accelerated Aging of Medical Devices;
医疗器械加速老化实验确定有效期的基本原理和方法
2.
Research advances in the accelerated aging methods of polymeric composites (PMC)are reviewed.
概述了聚合物基复合材料加速老化研究方法的进展,从试验方法、老化机理等方面着重介绍了湿热老化、腐蚀侵蚀和人工气候老化,总结了高置信度、高可靠度评估复合材料工作寿命的方法,并展望了复合材料加速老化研究方法。
3.
The accelerated aging experiments for PMMA specimens have been conducted for 70 days under the conditions of tap water air(50 ℃ temperature),and macro-mechanical characteristics of PMMA were tested at different time during the experiments,and structure difference were analyzed between samples before aging and after aging by methods of GPC and DSC.
研究是在自来水(50℃温度)条件下对有机玻璃做了70 d(天)左右的人工加速老化试验,然后对不同老化时间的有机玻璃试样进行了宏观力学性能测试,并进一步利用凝胶渗透色谱法(GPC)、示差扫描量热法(DSC)等手段,分析了老化前后有机玻璃试样的结构和组成差异,结合老化前后有机玻璃力学性能的变化,揭示了有机玻璃在自来水条件下的老化规律和老化机理。
补充资料：加速臭氧老化
分子式：
CAS号：
性质： 高分子材料在模拟强化大气臭氧的条件作用下产生的各种变化。臭氧是化学活性极高的物质，较分子氧更容易与含双键的高分子化合物发生化学反应。不饱和高分子化合物在应力作用下遇臭氧易产生垂直于应力方向的裂纹，称之臭氧龟裂。评价加速臭氧老化，通过臭氧老化试验进行。试验时使用臭氧老化箱，其臭氧浓度可分别为低、中、高三个范围。结果由试样外观、力学性能老化前后变化情况及龟裂程度等综合评价。
CAS号：
性质： 高分子材料在模拟强化大气臭氧的条件作用下产生的各种变化。臭氧是化学活性极高的物质，较分子氧更容易与含双键的高分子化合物发生化学反应。不饱和高分子化合物在应力作用下遇臭氧易产生垂直于应力方向的裂纹，称之臭氧龟裂。评价加速臭氧老化，通过臭氧老化试验进行。试验时使用臭氧老化箱，其臭氧浓度可分别为低、中、高三个范围。结果由试样外观、力学性能老化前后变化情况及龟裂程度等综合评价。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条