1) 2-tert-butylaminoethyl methacrylate
甲基丙烯酸叔丁基氨基乙酯
2) 2-tert-butylaminoethyl methacrylate
甲基丙烯酸-2-叔丁基氨基乙酯
3) N-allyl-N-(m-aminophenyl)methyl carbamate
N-烯丙基-N-间氨基苯甲基-氨基甲酸叔丁酯
1.
Then,nitro reduction and aliphatic amine protection was achieved in one pot synthesis and a new compound,N-allyl-N-(m-aminophenyl)methyl carbamate,was thus obtained with 57% yield.
以间硝基苯甲醛和烯丙基胺为原料,通过还原胺化反应制得N-烯丙基-间硝基苄胺,然后实现了硝基还原和脂肪胺选择性保护一锅法进行,以57%的总收率合成了新化合物N-烯丙基-N-间氨基苯甲基-氨基甲酸叔丁酯。
4) poly(tert-butylmethacrylate)
聚甲基丙烯酸叔丁酯
1.
Core/shell composite microparticles with silica nanoparticle as core and crosslinked poly(tert-butylmethacrylate) as shell were prepared by seed-emulsion polymerization utilizing 3-(trimethoxysilyl)propyl methacrylate(MPS) modified silica particles as seeds,tert-butylmethacrylate as monomer and sodium dodecyl sulfate(SDS) as emulsifier.
以甲基丙烯酸-3-(三甲氧基硅基)丙酯(MPS)修饰的SiO2胶体粒子为种子,甲基丙烯酸叔丁酯(tBMA)为单体、十二烷基硫酸钠(SDS)为乳化剂,采用种子乳液聚合法制备了SiO2/聚甲基丙烯酸叔丁酯的核壳复合微粒。
2.
The aim to synthesize the composite microparticles based on silica as core and crosslinked poly(tert-butylmethacrylate) as shell in this work, is to prepare the inorganic/organic core/shell composite microparticles whose shells are composed of crosslinked poly(methacrylic acid) by transforming poly(tert-butylmethacrylate) into poly(methacrylic acid) by hydrolysis.
本文采用种子乳液聚合法制备内核为二氧化硅、壳层为具有交联结构的聚甲基丙烯酸叔丁酯的核壳复合微粒,目的是想通过水解,使聚甲基丙烯酸叔丁酯转变为聚甲基丙烯酸,最后得到壳层为交联聚甲基丙烯酸的无机/有机核壳复合微粒。
5) tert-butyl-α-methacrylate
α-甲基丙烯酸叔丁酯
6) tert-butyl methacrylate
甲基丙烯酸叔丁酯
1.
In this study,a homopolymer and a series of copolymers of tert-butyl methacrylate(TBMA) with methacrylic acid(MAA) and styrene(St) were synthesized.
本研究合成了甲基丙烯酸叔丁酯(TBMA)的均聚物及其与甲基丙烯酸(MAA)、苯乙烯(St)的共聚物,并与二乙烯基醚(BPA-DEVE)和光生酸剂(PAG)构成光敏成像体系。
2.
Macro-intermediate with Br-end Poly(tert-butyl methacrylate)(PtBMA-Br) was synthesized by Atom Transfer Radical Polymerization(ATRP),with ethyl-2-bromopropionate as initiator,a compound system of CuCl/ N,N,N′,N″,N″-penta-methyldiethylenetri-amine(PMDETA) as catalyst.
以α-溴代丙酸乙酯(EPN-Br)为引发剂,氯化亚铜(CuCl)与N,N,N′,N″,N″-五甲基二亚乙基三胺(PMDETA)组成的混合体系为催化剂,使甲基丙烯酸叔丁酯(tBMA)进行原子转移自由基聚合(ATRP),得到了端基为溴原子的聚甲基丙烯酸叔丁酯大分子中间体PtBMA-Br。
3.
The diblock copolymer of styrene and tert-butyl methacrylate was synthesized by anionic polymerization at 10 ℃.
在 10℃下 ,采用阴离子聚合方法合成相对分子质量、嵌段组成均可控且相对分子质量分布窄的苯乙烯 -甲基丙烯酸叔丁酯嵌段共聚物 ,对所得共聚物进行了IR、NMR、TG、TEM等表征 ,表明共聚物为嵌段结
补充资料：甲基丙烯酸叔丁基氨基乙酯
分子式： CH2＝C(CH3)COOCH2CH2NHC(CH3)3
CAS号：
性质：又称甲基丙烯酸叔丁基氨基乙酯。液体。熔点<-70℃。沸点93℃(1.33kPa，10mmHg)。闪点11℃(开杯)。相对密度0.914。折射率1.4400。溶于一般有机溶剂，微溶于水。易聚合，通常加入0.1％氢醌单甲醚作阻聚剂。由甲基丙烯酸甲酯和叔丁基氨基乙醇进行酯交换反应制得。也可由甲基丙烯酸直接和叔丁基氨基乙醇进行酯化反应制得。用作高分子材料改性剂。制备热固性涂料、黏合剂等的交联剂以及润滑油添加剂和颜料着色剂等。
CAS号：
性质：又称甲基丙烯酸叔丁基氨基乙酯。液体。熔点<-70℃。沸点93℃(1.33kPa，10mmHg)。闪点11℃(开杯)。相对密度0.914。折射率1.4400。溶于一般有机溶剂，微溶于水。易聚合，通常加入0.1％氢醌单甲醚作阻聚剂。由甲基丙烯酸甲酯和叔丁基氨基乙醇进行酯交换反应制得。也可由甲基丙烯酸直接和叔丁基氨基乙醇进行酯化反应制得。用作高分子材料改性剂。制备热固性涂料、黏合剂等的交联剂以及润滑油添加剂和颜料着色剂等。