1) gold-silver-copper-manganese-gadolinium alloy
金银铜锰钆合金
2) silver-copper-manganese alloys
银铜锰合金
3) gold-silver-copper-manganese alloys
金银铜锰合金
4) silver-manganese alloys
银锰合金
5) Mn-Cu alloy
锰铜合金
1.
The dynamics characters of axis sleeve made of the new Mn-Cu alloy is investigated, which is used as absorber in the high-speed rotary fusee-testing machine.
根据基础激振—共振质量法测试原理设计专用的实验测试系统,对作为高速旋转引信实验机减振部件使用的新型锰铜合金圆环类部件进行动力学特性测试。
2.
Variance of phyxics and mechanical property of Steel and Mn-Cu alloy are enormous, obtain good joint is difficult by conventional welding method.
钢与ZMnD-1J锰铜合金在物理、力学性能方面差异巨大,用传统的方法焊接,难以得到性能良好的接头。
6) Ag-Cu alloy
银铜合金
1.
This paper summarizes the usual technology methods of producing Ag-Cu alloy contact wire used for electrical railway,explains the necessity to develop new technology,develops a new method of producing Ag-Cu alloy contact wire,that is continuous extrusion method.
概述了电气化铁路银铜合金接触线的常用工艺方法,说明了研究新的接触线制造工艺的必要性,并提出了新的银铜合金接触线制造方法———连续挤压法。
2.
The technological specificity of the continuous extrusion forming for Ag-Cu alloy and the effects of several process parameters, such as extrusion temperature, extrusion wheel rate, extrusion ratio and flash gap, on the process were analyzed and discussed.
分析讨论了银铜合金连续挤压工艺特点及挤压温度、挤压轮转速、挤压比、溢料间隙对连续挤压制品质量的影响。
补充资料：金银铜锰钆合金
分子式：
CAS号：
性质：金基添加银、铜、锰和钆的五元合金，钆可提高合金的硬度、抗拉强度、耐磨性、耐蚀性和再结晶温度。AuAgCuMnGd33.5-3-2.5-0.5的抗拉强度588.4MPa，维氏硬度1216MPa，电阻系数24×10-2Ω·mm2/m，电阻温度系数0.17×10-4/℃，再结晶温度450～500℃。真空中频炉充氩保护熔炼，铸锭经由冷加工成材，保护气氛下进行中间退火。用作高耐磨的精密电阻材料，可代替PtIr10合金。
CAS号：
性质：金基添加银、铜、锰和钆的五元合金，钆可提高合金的硬度、抗拉强度、耐磨性、耐蚀性和再结晶温度。AuAgCuMnGd33.5-3-2.5-0.5的抗拉强度588.4MPa，维氏硬度1216MPa，电阻系数24×10-2Ω·mm2/m，电阻温度系数0.17×10-4/℃，再结晶温度450～500℃。真空中频炉充氩保护熔炼，铸锭经由冷加工成材，保护气氛下进行中间退火。用作高耐磨的精密电阻材料，可代替PtIr10合金。