1) open splice
接头裂开
2) cold-upsetting cracks
镦头开裂
3) bolt head rupture
帽头开裂
4) head rupture
头部开裂
1.
The problem of head rupture during the kinds of easily cutting stainless steels rolling such as 303Cu is solved by using this system.
该系统的使用,能有效解决易切削不锈钢303Cu等钢种轧制过程中易发生头部开裂现象,提高生产效率和产品质量。
5) cleavage joint
劈裂接头
1.
The analysis of stress distribution in bi-adhesives bonded cleavage joints;
混合胶接劈裂接头胶层中应力分布的数值分析
2.
Based on the finite element analysis software ANSYS,the elasto-plastic finite element numerical simulation and analysis for normal stress and shear stress distribution in the middle of adhesive layer of steel cleavage joints were carried out.
采用有限元分析软件ANSYS,对钢制劈裂接头上胶层中部的正应力和剪切应力的分布进行了弹塑性有限元数值模拟与分析。
6) joint broken
接头断裂
1.
The paper analyzed the cause of the joint failure in conveyor steel core belt base on the alternant bending stress and tension stress Special means were made to the failure of real joints for the test and observation With the analysis, the test results can provide a predicted basis and means to the joint broken of the belt in operatio
从交变弯曲应力和拉应力的角度对钢芯输送带接头损坏的原因进行了分析 ,并采用特殊的手段对实际接头进行了破断试验观测 ,通过对试验结果的分析 ,为钢芯输送带使用中接头断裂提供了预报的依据和手段。
补充资料：接头裂开
分子式：
CAS号：
性质：又称开缝、开胶。指外胎的胎面、胎侧、气密层(或内衬层)以及内胎、垫带的接头处，在橡胶未能正确黏结密合时，导致硫化后接头处脱开的现象。
CAS号：
性质：又称开缝、开胶。指外胎的胎面、胎侧、气密层(或内衬层)以及内胎、垫带的接头处，在橡胶未能正确黏结密合时，导致硫化后接头处脱开的现象。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。