1) PB
聚-1-丁烯
2) polybutene-1
聚丁烯-1
1.
Synthesis of high isotactic polybutene-1;
高等规度聚丁烯-1的合成
2.
The effect of molecular structure of polybutene-1 on crystallization morphology;
聚丁烯-1分子结构对结晶的影响
3.
Recent Advances in the Preparation of Polybutene-1;
聚丁烯-1制备研究进展
3) Poly-1-butene
聚丁烯-1
1.
Effects of CaCO_3 on the Properties of Waterproof Roll of Poly-1-butene Thermoplastic Elastomer;
CaCO_3填料对聚丁烯-1热塑性弹性体防水卷材性能的影响
2.
Effects of Carbon Black on the Properties of the Waterproof Roll of Poly-1-butene Thermoplastic Elastomer;
炭黑对聚丁烯-1热塑性弹性体防水卷材性能的影响
4) poly(1-butene)
聚1-丁烯
1.
Effect of aging on polymerizing poly(1-butene) with supported titanium catalyst;
陈化方式对负载钛催化合成聚1-丁烯的影响
2.
Polymerization of 1-butene in the presence of supported titanium catalyst and Al(i-Bu)3. Structure and properties of poly(1-butene);
负载钛-三异丁基铝体系催化1-丁烯聚合 Ⅱ.聚1-丁烯的结构与性能
3.
Synthesis of high isotactic poly(1-butene) at low temperature
低温合成高等规度聚1-丁烯
5) PB_(-1)
聚丁烯_(-1)
补充资料:聚-1-丁烯
分子式:
CAS号:
性质: 由1-丁烯均聚或与少量其他α-烯烃共聚而成的一种热塑性树脂。结晶度50%~55%,密度0.91~0.915g/cm3。拉伸强度28~32MPa,悬臂梁缺口冲击不断,邵氏硬度D32~55。脆化温度<-187℃,维卡软化点113~121℃。有突出的耐环境应力开裂性,而且抗蠕变性、耐磨性、耐化学药品性、耐热性好,可在-30~100℃下长期使用。可采用齐格勒-纳塔催化剂,经浆液聚合、本体聚合或气相聚合制得。在加工成制品时存在晶形转变问题。在室温和常压下,大约5~7天后才逐渐由不稳定的II型晶态转变成稳定的I型晶态。主要用于热水管、工业用管、气体管等,用以代替铜管或铝管,也用于薄膜,板材、容器、密封件、单丝等。
CAS号:
性质: 由1-丁烯均聚或与少量其他α-烯烃共聚而成的一种热塑性树脂。结晶度50%~55%,密度0.91~0.915g/cm3。拉伸强度28~32MPa,悬臂梁缺口冲击不断,邵氏硬度D32~55。脆化温度<-187℃,维卡软化点113~121℃。有突出的耐环境应力开裂性,而且抗蠕变性、耐磨性、耐化学药品性、耐热性好,可在-30~100℃下长期使用。可采用齐格勒-纳塔催化剂,经浆液聚合、本体聚合或气相聚合制得。在加工成制品时存在晶形转变问题。在室温和常压下,大约5~7天后才逐渐由不稳定的II型晶态转变成稳定的I型晶态。主要用于热水管、工业用管、气体管等,用以代替铜管或铝管,也用于薄膜,板材、容器、密封件、单丝等。