1.
The fractography of PBT at different temperatures was analyzed, the fractography features of PBT fracture arc stripe were concluded, the total number, dimension of feature zone and roughness of arc stripe were studied in quantification, the mechanism of arc pattern was also discussed.
分析了不同温度下聚对苯二甲酸丁二醇酯(PBT)的断口形貌,总结了PBT断口弧形条纹的形貌特征,定量研究了弧形条纹数量、特征区尺寸及表面粗糙度的变化规律,并对其形成机理进行了探讨。
2.
POE-g-GMA and PBT/POE-g-(GMA-coSt) were prepared by melt grafting in the twin screw extruder.
在双螺杆挤出机上采用熔融接枝法制备了POE-g-GMA和POE-g-(GMA-co-St),考察了POE、POE-g-GMA和POE-g-(GMA-co-St)对聚对苯二甲酸丁二醇酯(PBT)的增韧作用。
3.
The effect of the mass content of glass microbeads (GB) on the melt rheological and mechanical properties of PBT/short glass fiber(GF)composite was studied.
研究了玻璃微珠(GB)用量对聚对苯二甲酸丁二醇酯(PBT)/短玻纤(GF)复合材料熔体流变性和力学性能的影响。
补充资料：聚对苯二甲酸(丁二醇-乙二醇)酯
分子式：
CAS号：
性质： 又称对苯二甲酸(丁二醇-乙二醇)共聚酯。同时含有对苯二甲酸丁二酯和对苯二甲酸乙二酯结构，且以前者含量居多的热塑性聚酯。同时兼有PBT和PET两者的特性，但可纺性、卷装成型性、染色性和冲击强度均优于二者。相对密度1.30～1.35。熔融温度210～215℃。拉伸强度50～55MPa。弯曲强度80～100MPa。冲击强度(缺口)7.0kJ/m(无缺口时不断)。由对苯二甲酸丁二酯与对苯二甲酸乙二酯共缩聚制得。目前主要用作合成纤维的原料，但有用作工程塑料的前景。