1) polyimide foam
聚酰亚胺泡沫塑料
2) polyamide foam
聚酰胺泡沫塑料
3) Thermoplastic polyimide foam
热塑性聚酰亚胺泡沫
4) poly-aminoester foamed plastics
聚酰胺酯泡沫塑料
5) poly(carbodiimide)foam
聚碳化二亚胺泡沫塑料
6) polyimide foam
聚酰亚胺泡沫
1.
The effect of sparkling technology on polyimide foam structure;
发泡工艺条件对聚酰亚胺泡沫结构的影响
2.
The closed cell polyimide foams were fabricated by foaming the precursor balloons,and the foams\' acoustic absorption properties were tested.
采用前驱体微球法制备闭孔聚酰亚胺泡沫,并对其吸声性能进行了研究。
3.
Experimental studies were undertaken to investigate glass transition temperature,thermal conductivity at static temperature and performance of thermal insulation at dynamic temperature of 4 kinds for aromatic polyimide foams by DMTA and self-made apparatus.
利用DMTA和自制热导测试仪测试了4种自制芳香族聚酰亚胺泡沫的玻璃化转变温度(Tg)、静态温度下的热导率(λ)和动态温度作用下的隔热性能;分析了一定厚度的聚酰亚胺泡沫的密度和温度影响热导率的规律;考察了聚酰亚胺泡沫在动态温度下的隔热性能。
补充资料：聚酰亚胺泡沫塑料
分子式：
CAS号：
性质： 以聚酰亚胺为主要成分制备的一类泡沫塑料。Imi-Tech公司专利。由二苯甲酮四羧酸二酐、二元胺和发泡剂制得的硬质泡沫塑料，具有优良的耐热性和高温力学强度。发泡工艺与一般泡沫塑料的制备方法相似，还可利用聚酰胺酸溶液挥发溶剂进行发泡和酰亚胺化过程中脱出水分子而发泡。聚酰亚胺泡沫塑料具有优良的机械性能、热稳定性高，230℃下空气中老化14天失重2％、压缩强度不变，450℃下老化10min失重6％。室温下相对介电常数为2～3，介质损耗因数为0.002～0.02(0.1～1000Hz)。水蒸气渗透率低。适用作飞机和航天器隔热、隔音、减震的各种隔板和结构部件，也可用作电绝缘材料。
CAS号：
性质： 以聚酰亚胺为主要成分制备的一类泡沫塑料。Imi-Tech公司专利。由二苯甲酮四羧酸二酐、二元胺和发泡剂制得的硬质泡沫塑料，具有优良的耐热性和高温力学强度。发泡工艺与一般泡沫塑料的制备方法相似，还可利用聚酰胺酸溶液挥发溶剂进行发泡和酰亚胺化过程中脱出水分子而发泡。聚酰亚胺泡沫塑料具有优良的机械性能、热稳定性高，230℃下空气中老化14天失重2％、压缩强度不变，450℃下老化10min失重6％。室温下相对介电常数为2～3，介质损耗因数为0.002～0.02(0.1～1000Hz)。水蒸气渗透率低。适用作飞机和航天器隔热、隔音、减震的各种隔板和结构部件，也可用作电绝缘材料。