1) polyamide/styrene-maleic anhydride copolymer blend
聚酰胺/苯乙烯-马来酸酐共聚物共混物
2) PA/SMA blend
聚酰胺/苯乙烯-马来酸酐共聚物共混物
3) polyimide
聚酰
4) co-polyamide
共聚酰胺
1.
Polyoxymethylene (POM) was blended with co-polyamide (COPA) as a formaldehyde absorber.
用 2 2 0℃等温热失重法通过对热失重率和热失重速率的测试研究了共聚酰胺 (COPA)作为甲醛吸收剂对聚甲醛 (POM )热稳定性的影响。
5) Polyimide
聚酰亚胺
1.
Synthesis and properties of sulfonyl-substituted polyimides with high refractive indices and high transparency;
砜基取代高折射率高透明性聚酰亚胺的合成与性能
2.
Study on polyimide resin modified by nano-Si_3N_4 for diamond tools;
金刚石磨具纳米Si_3N_4改性聚酰亚胺树脂结合剂研究
3.
Effect of coupling agent on microstructure and properties of polyimide/SiO_2 hybrid membrane;
偶联剂对聚酰亚胺/SiO_2杂化膜性能的影响
6) polyamide
聚酰胺
1.
Study on the Toughening and Thermal Stabilization of Polyamide on Polyoxymethylene;
聚酰胺对聚甲醛的增韧及热稳定作用研究进展
2.
Dyeing of polyamide with ultra-high wet fastness;
具有超高湿色牢度的聚酰胺染色
3.
Theoretical study of vibrational spectra of aliphatic polyamide by density functional theory;
脂肪族聚酰胺振动光谱的密度泛函理论研究
参考词条
补充资料：聚酰胺/苯乙烯-马来酸酐共聚物共混物
分子式：
CAS号：
性质： 苯乙烯-马来酸酐共聚物添加到PA中，由于其酸酐与PA分子末端氨基反应可形成接枝共聚物，所以这种共混物具有稳定的均匀细分散形态结构，其悬臂梁冲击强度(无缺口)达到392J/m，但热变形温度为112℃，拉伸强度为71MPa，均不突出。日本电气化学株式会社以苯乙烯-N-苯基马来酰亚胺共聚物(简称IP树脂)与PA共混得到一种新型PA合金。IP树脂的玻璃化温度达到200℃，分解温度则为350°以上，PA/IP树脂共混物具有非常好的耐热和耐化学药品性，制品在180℃处理2h仍不变形；其耐候性、耐磨耗性、装饰性、成型加工性等也均比较良好。
CAS号：
性质： 苯乙烯-马来酸酐共聚物添加到PA中，由于其酸酐与PA分子末端氨基反应可形成接枝共聚物，所以这种共混物具有稳定的均匀细分散形态结构，其悬臂梁冲击强度(无缺口)达到392J/m，但热变形温度为112℃，拉伸强度为71MPa，均不突出。日本电气化学株式会社以苯乙烯-N-苯基马来酰亚胺共聚物(简称IP树脂)与PA共混得到一种新型PA合金。IP树脂的玻璃化温度达到200℃，分解温度则为350°以上，PA/IP树脂共混物具有非常好的耐热和耐化学药品性，制品在180℃处理2h仍不变形；其耐候性、耐磨耗性、装饰性、成型加工性等也均比较良好。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。