1) alumina modulus
铝氧率
2) extraction ratio of alumina
氧化铝浸出率
1.
Effect of different calcination temperature on structure and extraction ratio of alumina from Kaolinite of Inner Mongolia was studied in this article.
考察了煅烧温度对内蒙煤系高岭土结构及其氧化铝浸出率的影响。
3) low alumina iron modulus proportion
低铝氧率配比
4) dissolution of suspension revert
氧化铝产出率
5) extraction rate of alumina
氧化铝提取率
1.
The extraction rate of alumina from refuse is related to the formulation for preparing the mixture of refuse, limestone and soda ash as well as the technological parameters.
研究的结果表明，混合物料制备时，采用分子比ＭＮａ２ＯＭＡｌ２Ｏ３为１和ＭＣａＯＭＳｉＯ２为２的配料比例，控制物料的体积平均粒径为００６～００７ｍｍ，并使物料在１０４０℃下烧结８０ｍｉｎ，可获得合理的氧化铝提取率为８０％～８５％。
6) Al2O3 leaching rate
氧化铝溶出率
1.
At the same time,the infulence of Al2O3 leaching rate at middle grade bauxite contain different sulfur contents is also studied.
对纯碱烧结法烧结条件进行了研究,考查碱比、烧结温度、烧结时间等对氧化铝溶出率的影响。
补充资料：铝氧率
分子式：
CAS号：
性质：又称铝率。用AM(P)或IM表示。是硅酸盐水泥生产中控制生、熟料中酸性氧化物之间比例的参数之一，表示生、熟料中氧化铝和氧化铁质量百分数之比。计算式为AM(P)=，一般为0.8～1.7。铝氧率也表示熟料熔剂矿物中铝酸三钙和铁铝酸四钙的比例。铝氧率的高低，在一定程度上反映了水泥煅烧过程中高温液相的黏度。铝氧率高，熟料中铝酸三钙多，铁铝酸四钙含量相对降低，液相黏度大，物料难烧，硅酸三钙的生成速度变慢；反之，液相黏度低，对硅酸三钙的形成有利，熟料易烧成，但烧结范围变窄，窑内易结大块，不利于窑的操作。
CAS号：
性质：又称铝率。用AM(P)或IM表示。是硅酸盐水泥生产中控制生、熟料中酸性氧化物之间比例的参数之一，表示生、熟料中氧化铝和氧化铁质量百分数之比。计算式为AM(P)=，一般为0.8～1.7。铝氧率也表示熟料熔剂矿物中铝酸三钙和铁铝酸四钙的比例。铝氧率的高低，在一定程度上反映了水泥煅烧过程中高温液相的黏度。铝氧率高，熟料中铝酸三钙多，铁铝酸四钙含量相对降低，液相黏度大，物料难烧，硅酸三钙的生成速度变慢；反之，液相黏度低，对硅酸三钙的形成有利，熟料易烧成，但烧结范围变窄，窑内易结大块，不利于窑的操作。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。