1) lithium manganese ferrite
锂锰铁氧体
2) Li-Mn rectangular loop ferrite
锂-锰矩磁铁氧体
3) Li-ferrite
锂铁氧体
1.
The Cu-Ti co-metal wave-guide films on Li-ferrite material surface were made by a magnetron sputtering deposition.
采用磁控溅射镀膜方法,在锂铁氧体材料表面,制备了Cu-Ti复合金属波导膜系。
2.
The calculated results showed that the effective magnetic anisotropy constants of ultrafine particles were larger than the magnetocrystalline anisotropy constant of Li-ferrite.
结果发现，有效磁各向异性常数随粒度的减小而增大，微粉的有效磁各向异性常数大于锂铁氧体的磁晶各向异性常
4) lithium ferrite
锂铁氧体
1.
Influence of Dy_2O_3 Dopant on Microwave Absorption Properties Of Nanocrystalline Lithium Ferrite Powders;
Dy_2O_3掺杂对纳米锂铁氧体微波吸收特性的影响
5) Li ferrite
锂铁氧体
1.
The Li ferrite materials were prepared by conventional ceramic technology.
结果表明,添加适量超细球状Bi2O3粉可有效抑制Li的挥发,同时引入Zn2+、、Ti4+、、Mg2+、、Mn2+等金属离子可将锂铁氧体的烧结温度降低至900℃以下,从而实现与银内电极的低温共烧。
2.
The Cu Ti co metal wave guide films on Li ferrite material surface have been made by magnetron sputtering deposition.
采用磁控溅射镀膜方法 ,在锂铁氧体材料表面 ,制备了 Cu- Ti复合金属波导膜系。
6) manganese ferrite
锰铁氧体
补充资料：锂锰铁氧体
分子式：Li0.5Fe2.2～2.4Mn0.1～0.27O4
CAS号：
性质：以铁和锂氧化物为主同时掺锰的复合氧化物矩磁材料。立方晶系尖晶石结构。具有较高的饱和磁感应强度和矫顽力，居里点高约600℃，温度系数小。采用高温固相烧结法制备，主要用作宽温度范围(-55～125℃)磁心存储元件材料。
CAS号：
性质：以铁和锂氧化物为主同时掺锰的复合氧化物矩磁材料。立方晶系尖晶石结构。具有较高的饱和磁感应强度和矫顽力，居里点高约600℃，温度系数小。采用高温固相烧结法制备，主要用作宽温度范围(-55～125℃)磁心存储元件材料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。