1) massive crystalline graphite
块状晶质石墨
2) blocky graphite
块状石墨
3) Scaly graphite
晶质石墨
4) chunky graphite
碎块状石墨
1.
According to stress of graphite austenite eutectic cell during solidification, the caues of chunky graphite of hot spot and some factors are analysed in this article.
本文从球墨铸铁石墨———奥氏体共晶团形成及长大过程中的应力出发 ,分析了大断面球铁热节处非球形石墨—碎块状石墨的形成原因及若干影响因素 ,提出了防止措施。
2.
The nesnlts show that St will fiercely promote the formation of chunky graphite when more than 2.
１％时，强烈促进碎块状石墨的形成，防止碎块状石墨的关键是减少Ｓｉ，使球铁碳当量不超过共晶碳当量。
3.
Presence of chunky graphite seems to be more of a problem in ferritic,high Si and austenitic ductile iron.
碎块状石墨(chunky graphite)是厚大断面球墨铸铁件常见的缺陷之一,尤其在铁素体球铁、高w(Si)量以及奥氏体球墨铸铁中较为严重,它会明显影响铸件的力学性能,应尽可能避免或控制。
5) quasi-flake graphite
似块状石墨
6) Aphanitic graphite
隐晶质石墨
1.
Study on the ultrafine aphanitic graphite particles fabricated with stirred mill;
搅拌磨制备隐晶质石墨超细粉体的研究
2.
Kinetic equation in the baking process of purifying aphanitic graphite were researched.
研究了隐晶质石墨的提纯工艺中焙烧动力学方程。
3.
In the article, the process conditions of wet surface modification of aphanitic graphite are studied.
选用不同的偶联剂对隐晶质石墨粉进行表面化学改性。
补充资料：块状晶质石墨
分子式：
CAS号：
性质：又称致密结晶状石墨或聚晶质石墨。其晶体呈杂乱或放射状。含石墨量一般大于60％，有时达80％～90％。平均直径一般大于0.1mm。按晶体大小可分为粗粒和细粒(平均粒径小于0.1mm)。产于火成岩(霞石正长岩)和片麻岩中，呈株状、巢状、脉状分布。其润滑性、柔韧性等不如鳞片状石墨好。可用作一般石墨的原料。
CAS号：
性质：又称致密结晶状石墨或聚晶质石墨。其晶体呈杂乱或放射状。含石墨量一般大于60％，有时达80％～90％。平均直径一般大于0.1mm。按晶体大小可分为粗粒和细粒(平均粒径小于0.1mm)。产于火成岩(霞石正长岩)和片麻岩中，呈株状、巢状、脉状分布。其润滑性、柔韧性等不如鳞片状石墨好。可用作一般石墨的原料。