The results showed that the t_(10)and t_(90)of rubber compound extended a little by using superfine active kaolin partly instead of carbon black in inner ply and outer ply compounds,and the physical properties of vulcanizate and H pull-out after aging changed little;the endu-rance of finished tire improved and the cost of rubber compound reduced.
结果表明,在内层和外层帘布胶中以超细活性高岭土部分替代炭黑后,胶料的t10和t90稍有延长,硫化胶的物理性能及老化后H抽出力基本相当;成品轮胎耐久性能提高,胶料成本降低。
2.
The results showed that the scorch time extended,the curing speed reduced,the anti-reversion improved,and the better tensile,elongation and tear properties were obtained using TBSI instead of TBBS by equal weight in the upper bead filler compound;and the scorch time extended,t_(90) reduced,the permanent tensile set decreased and the H pull-out changed little using 1 phr of TBSI instead of 1.
在胎体胶配方中以 1份促进剂TBSI替代 1 2 5份促进剂DZ ,胶料的焦烧时间延长 ,t90 缩短 ,硫化胶的拉断永久变形减小 ,H抽出力相当。
3) H pull-out force
H抽出力
1.
The results showed that when compared to the dry cobalt decanoate,the wet cobalt decanoate gave NR vulcanizate higher H pull-out force,lower H pull-out force loss after hot air aging and brine aging and similar physical properties.
结果表明,与干法工艺生产的癸酸钴相比,采用湿法工艺生产的癸酸钴可提高NR硫化胶的H抽出力,经热空气老化和盐水老化后硫化胶的H抽出力下降率较小,其它物理性能基本相当。
4) adhesion by H test
H抽出值
1.
Experiments on changing fomula of nylon6 dip solution find that there has a constant ratio betwen RFL viscosity and adhesion by H test of nylon6 dipped cord fabric.
通过对浸胶液处方的调整试验 ,发现RFL液粘度与帘子布H抽出值之间存在比例关系 ,从而可以用RFL液粘度推算帘子布的H抽出值大
5) H-test
"H"抽出
6) MH sampling
M-H抽样
补充资料：H抽出
分子式：
CAS号：
性质：测定帘子线与橡胶间附着力的指标。黏着力大，帘子线(布)与橡胶的黏着性能良好。试验方法为将帘子线试样嵌入按配方制成的橡胶片内，在规定的压力、温度和时间内硫化，修整成规定规格的“H”型试片，用强力机中测定从试片中抽出帘子线的力。
CAS号：
性质：测定帘子线与橡胶间附着力的指标。黏着力大，帘子线(布)与橡胶的黏着性能良好。试验方法为将帘子线试样嵌入按配方制成的橡胶片内，在规定的压力、温度和时间内硫化，修整成规定规格的“H”型试片，用强力机中测定从试片中抽出帘子线的力。