1) Zirconium chloride basic
氯化锆酰
2) zirconium oxychloride
氯氧化锆
1.
Study on preperations of crystalline layered sodium disilicate with wastes of zirconium oxychloride
氯氧化锆废弃物制备层状硅酸钠的研究
2.
ZnO green phosphor preparation process by the thermal oxidation of zinc sulfide with zirconium oxychloride as additive is investigated.
研究以氯氧化锆为添加剂的硫化锌热氧化法合成ZnO绿色荧光粉的过程。
3.
The acid property of zirconium oxychloride was characterized by means of DTA and FT-IR spectra of pyridine absorbed on the surface.
采用DTA和吸附吡啶的FT-IR表征氯氧化锆的表面酸性,用Hamm ett指示剂测定其酸强度,以催化合成环己酮2,3-丁二醇缩酮为探针反应优化缩酮反应条件,并考察它对其他缩酮反应的催化活性,比较了不同催化剂对缩酮活性的影响。
3) zirconium carbide
氧氯化锆
1.
20% was prepared from zirconium carbide by the process of alkali fusing,water washing,hydrochloric acid leaching and product crystallization.
以碳化锆为原料,采用碱熔-水洗-酸浸-结晶工艺制备氧氯化锆,制得的氧氯化锆产品中ZrO2含量达到36。
4) zirconium oxychloride
氧氯化锆
1.
The production of zirconium oxychloride and its application in new energy resource;
氧氯化锆的生产及其在现代新能源中的应用
2.
With zirconium oxychloride and γ-aminopropyltriethoxysilane(KH-550) as precursor, the hybrid film composed of zirconia and organosilicone was prepared on polycarbonate through co-condensation reactions by sol-gel method.
以氧氯化锆(ZrOCl_2·8H_2O)和γ-氨丙基三乙氧基硅烷(KH-550)为先驱体,采用溶胶-凝胶法通过共缩聚反应在聚碳酸酯(PC)板表面制备了锆/有机硅复合薄膜,采用TG/DTA、FTIR、UV-VIS、金相显微镜及铅笔硬度测试方法对复合薄膜的结构及性能进行表征。
3.
Through grinding in the mortar,the solid state zirconium oxychloride reacts with solid sodium hydroxide or hexamethylene tetramine or the mixture of sodium hydroxide and lithium carbonate,the zirconium hydroxide,which is the precursor of Nano ZrO_2 powder,is obtained.
通过在研钵内研磨,使固相的氧氯化锆分别与固相的氢氧化钠或六次甲基四胺或氢氧化钠和碳酸锂的混合研磨物发生反应,生成纳米二氧化锆粉体的前驱体氢氧化锆,然后中温(400℃)烧结制得纳米二氧化锆粉体,粒径约为10nm。
5) ZrOCl_2·8H_2O
氧氯化锆
1.
One-step hydrothermat method is that ZrOCl_2·8H_2O solution and ammonia water are mixed in proportion and then added directly into autoclave to reaction.
一步水热法是将氧氯化锆和氨水按比例混和后,直接加入高压反应釜中进行水热反应的工艺。
6) ZrOCl2
氧氯化锆
1.
This article describes the process flow of ZrOCl2 evaporation system.
介绍了氧氯化锆蒸发工艺流程,重点是蒸发系统设备设计选型及设备使用注意事项。
补充资料：氯化锆酰
分子式：ZrOCl2·8H2O
分子量：322.25
CAS号：13520-92-8
性质：白色或略带黄色的丝状或针状结晶。
制备方法：暂无
用途：其它锆产品的中间体，也作橡胶添加剂，油漆催干剂等。
分子量：322.25
CAS号：13520-92-8
性质：白色或略带黄色的丝状或针状结晶。
制备方法：暂无
用途：其它锆产品的中间体，也作橡胶添加剂，油漆催干剂等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。