1) Lead stearate, dibasic
二盐基硬脂酸铅
2) Lead stearate,dibasic
二盐基性硬脂酸铅
3) lead stearate
硬脂酸铅
1.
Study on the production of lead stearate using waste material containing lead;
含铅废渣生产硬脂酸铅的研究
2.
Preparation and characterization of RDX/lead stearate composite particles;
RDX/硬脂酸铅复合粒子的制备及其性能表征
3.
It was found that the reaction of synthesis of lead stearate by direct method in aqueous medium could be accelerated markedly by ammonium salts.
研究发现铵盐对水介质直接法合成硬脂酸铅反应具有显著的催化加速作用。
4) acetoxy stearate
乙酸基硬脂酸盐
5) aqua cera
二甘醇硬脂酸盐
6) Lead oxide phosphite hydrate
二盐基亚磷酸铅
1.
Lead hydrogen phosphite superfine powder, lead oxide phosphite hydrate superfine powder and tribasic lead sulfate superfine powder were prepared by micro-liquid-phase synthesis method (MLPS method) in this paper.
本文采用微液相合成法制备了亚磷酸铅、二盐基亚磷酸铅和三盐基硫酸铅超细粉末，以氧化铅和亚磷酸或硫酸为原料，以醋酸为催化剂，在室温下充分混合、研磨几十分钟，干燥后即可得到产物。
补充资料：二盐基硬脂酸铅
分子式：C36H70O6Pb3
分子量：1220.49
CAS号：56189-09-4
性质：白色粉末。相对密度2.15，熔点>280℃（280-300℃分解），折光率1.60。溶于乙醚，不溶于水。
制备方法：由硬脂酸钠与乙酸铅反应而得。
用途：该品为聚氯乙烯稳定剂。铅稳定剂是聚氯乙烯最早使用的稳定剂，现在仍大量使用，我国的使用量约点全部稳定剂量的60%（不包括铅的皂类）。二盐基硬脂酸铅的热稳定性、电绝缘性、耐水性均以硬脂酸铅为优。常用于挤出制品，如管、波纹板、电线，也用于注射制品。
分子量：1220.49
CAS号：56189-09-4
性质：白色粉末。相对密度2.15，熔点>280℃（280-300℃分解），折光率1.60。溶于乙醚，不溶于水。
制备方法：由硬脂酸钠与乙酸铅反应而得。
用途：该品为聚氯乙烯稳定剂。铅稳定剂是聚氯乙烯最早使用的稳定剂，现在仍大量使用，我国的使用量约点全部稳定剂量的60%（不包括铅的皂类）。二盐基硬脂酸铅的热稳定性、电绝缘性、耐水性均以硬脂酸铅为优。常用于挤出制品，如管、波纹板、电线，也用于注射制品。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。