1) PPS
[英][,pi: pi: 'es] [美]['pi 'pi 'ɛs]
聚苯撑硫
2) Polyphenylene sulfide
聚苯撑硫
3) Poly(p-phenylene) polysulfide
多硫代聚苯撑
1.
Poly(p-phenylene) polysulfides (PPPS) were synthesized whose skeleton was conducting poly(p-phenylene)(PPP) with polysulfur side lines attaching to it by chlorination of PPP and subsequent sulfuration of poly(p-phenylene) chloride(PPPCl).
通过苯的聚合、聚苯撑氯代,氯代聚苯撑(PPPCl)的硫代三步合成了多硫代聚苯撑(PPPS),产物结构经13CNMR谱、IR光谱、Raman光谱和元素分析进行了鉴定,其中IR谱中461和615cm-1及Raman谱中470和666cm-1峰分别表明存在S—S键和C—S键,结合其它鉴定结果,证明终产物为多硫代聚苯撑。
4) Poly (metaphenylene sulfide-paraphenylene sulfide)
间苯撑硫醚-对苯撑硫醚共聚物
1.
As the modified material in the structure of PPS, Poly (metaphenylene sulfide-paraphenylene sulfide) copolymer (m-p-PPS) offsets the disadvantages such as poor toughness, great brittleness and indiscerptibility owing to some levels.
间苯撑硫醚-对苯撑硫醚共聚物(m-p-PPS)作为聚苯硫醚的主链结构改性材料,由于分子链结构中引入了间苯结构单元,分子链的柔性增强,从而弥补了聚苯硫醚韧性差、脆性大、难溶等缺点。
5) polyphenylene
[,pɔli'fi:nili:n]
聚苯撑
1.
Synthesis, Properties and Applications of the Polyphenylene;
聚苯撑的合成、性能及其应用
2.
Synthesis and characterization of polyphenylene copolymer composed of p-phenylene and m-phenylene units;
聚苯撑共聚物的合成与表征(英文)
6) polyparaphenylene
聚对苯撑
1.
Doping and Electric Conductivity of Polyparaphenylene;
聚对苯撑的掺杂和导电性能研究
补充资料：聚苯撑硫
聚苯硫醚是由对二氯苯与硫化钠反应制得。结构式为数均分子量为10000-50000。白色或朱黄色粉末。结晶度高，硬而脆，相对密度1．362。熔点275-290℃，玻璃化温度l50℃，700 ℃开始分解，热变形温度＞260℃，在400 ℃的空气或氮气中稳定，长期使用温度250 ℃。耐化学腐蚀性优异，对无机酸、碱、盐、有机酸、酯、酮、酯、醇、酚、脂肪烃、芳香烃、氯代烃等稳定。溶于氯代联苯，在170℃以下不溶于绝大多数溶剂。耐紫外线和60Co射线良好。
相对密度 1.34-1.36
吸水性(24h) ＜0．02％
拉伸强度 ＞96Mpa
伸长率 0．8％-1.3％
马丁耐热 ＞102℃
冲击强度(无缺口) ＞7.2kJ/m2
洛氏硬度 Rl21
极限氧指数 44～53％
相对密度 1.34-1.36
吸水性(24h) ＜0．02％
拉伸强度 ＞96Mpa
伸长率 0．8％-1.3％
马丁耐热 ＞102℃
冲击强度(无缺口) ＞7.2kJ/m2
洛氏硬度 Rl21
极限氧指数 44～53％
说明：补充资料仅用于学习参考，请勿用于其它任何用途。