1) glass-mat lamination sheet
玻璃毡层压板
2) glass cloth laminated sheet
玻璃布层压板
1.
The synthesis of benzoxazine-imide resin was studied,with which the glass cloth laminated sheet was made.
研究苯并噁嗪亚胺树脂的合成工艺,并利用其制备玻璃布层压板,经对该产品的性能进行全面测试。
2.
The paper descripes the development of class F high Strength epoxy glass cloth laminated sheet.
论文介绍了 F级高强度环氧玻璃布层压板的研制情况 ,研究了环氧树脂胶粘剂的合成 ,玻璃布层压板的制备工艺 ,原材料的影响因素及层压板性能。
3.
Abstract; The paper describes the synthesis of diphenylether resin modified with benzoxazine, and the method of making glass cloth laminated sheet with the resin.
论文介绍了一种改性二苯醚树脂的合成及其玻璃布层压板的制备方法,并对其性能进行了全面测试。
3) glass cloth laminated sheets
玻璃布层压板
1.
Study on aralkyl-phenol resin and the glass cloth laminated sheets;
芳烷基酚树脂及其玻璃布层压板的制备
2.
Study on aralky-phenol polyamide-imide resin and the glass cloth laminated sheets;
芳烷基酚聚酰胺玻璃布层压板的研制
4) glass cloth laminate
玻璃布层压板
1.
A new glass cloth laminate was prepared by using benzoxazine as liquid cement, alkali-free glass cloth as backing material, and treating with cement dipping, baking and pressing.
并以苯并恶嗪预聚体为胶液、无碱玻璃布为基材 ,经浸胶、烘焙、压制制得一种玻璃布层压板。
6) glass-cloth laminate
玻璃布层压板
1.
Therefore, a new glass-cloth laminate was prepared via ring-opening polymeriaztion ofbenzoxazine with no by-product under the processing condition of heating at 180 C andpresure of 6 MPa a for 4 hours.
以酚类化合物、甲醛和胺类化合物为原料合成含苯并恶嗪环结构的树脂溶液，用其浸渍玻璃布，在热压下苯并恶嗪发生开环聚合，从而制得一种新型开环聚合酚醛树脂基玻璃布层压板（ＭＤＡＰＦ-２-ＧＦ）。
2.
A new lower cost phenolic-basis glass-cloth laminate (ALPF/GF) has been prepared through ring-opening polymerization from the benzoxazine precursor synthesized by phenol.
性能测试表明,玻璃布层压板的耐电弧性达183s,氧指数为52,在155℃的弯曲强度为350MPa,其弯曲强度保持率达59％,而电性能在155℃保持良好,适于用作155℃使用的耐高温结构材料和电绝缘材料。
补充资料：乳化沥青玻璃毡片
分子式：
CAS号：
性质：又称乳化沥青玻璃毡片。是用中级定长玻璃纤维铺制成的毡状薄片，与乳化沥青配合制成的一种防水卷材。其抗拉强度高于500号纸胎油毡，柔韧性好，耐腐蚀性强，耐久性比普通油毡高一倍以上。耐热度在80℃温度下无流淌现象。做成二毡三油防水层(包括粘砂子的保护层)，用量3～4kg/m2。适用于屋面及地下工程作防水卷材。
CAS号：
性质：又称乳化沥青玻璃毡片。是用中级定长玻璃纤维铺制成的毡状薄片，与乳化沥青配合制成的一种防水卷材。其抗拉强度高于500号纸胎油毡，柔韧性好，耐腐蚀性强，耐久性比普通油毡高一倍以上。耐热度在80℃温度下无流淌现象。做成二毡三油防水层(包括粘砂子的保护层)，用量3～4kg/m2。适用于屋面及地下工程作防水卷材。