1) silane graft PE
硅烷接技聚乙烯
3) silane melt grafting of Polyethylenes
聚乙烯熔融接枝硅烷
4) Polyvinylsilazane
聚乙烯基硅氮烷
1.
Polyvinylsilazane (PVSZ) is a well known ceramic precursor for the fabrication of high performance ceramic structures which are involved in harsh environments.
采用带丙烯酸酯基团的烯丙基溴化合物(4-溴丁烯酸乙酯)和聚乙烯基硅氮烷发生取代反应,实现了丙烯酸酯基团在聚乙烯基硅氮烷主链上的链接。
5) silane crosslinked polyethylene
硅烷交联聚乙烯
1.
A special purpose grade of silane crosslinked polyethylene(PE Xb) for pipes was developed.
采用两步法研制开发出硅烷交联聚乙烯 (PE Xb)管材专用料 ,通过正交设计法探讨了硅烷交联聚乙烯的配方设计以及基础树脂、硅烷偶联剂等对其性能的影响和硅烷交联聚乙烯的耐热性能表征。
6) vinyl polysiloxane
乙烯基聚硅氧烷
1.
Its primary polymer is vinyl polysiloxane (VPS), which is cross-linked with hydride silicone activated by a platinum salt catalyst.
该材料基础聚合物为乙烯基聚硅氧烷(Vinyl Polysiloxane；VPS)，故简称VPS材料，其交联剂为含氢硅油，催化剂为铂盐或氯铂酸。
补充资料：硅烷接枝聚乙烯
分子式：
CAS号：
性质：主链侧具有～Si—O～Si～交联网状结构的一种化学改性聚乙烯。改善了普通聚乙烯的耐热性、耐应力开裂性、耐蠕变性、耐冲击性、耐磨性、耐油性及低温特性。密度0.929g/cm3，凝胶率68%。拉伸强度38MPa，弯曲弹性模量1600MPa，悬臂梁缺口冲击强度110J/m，热变形温度(1.87MPa)101℃，体积电阻率>106Ω·cm，介质损耗因数(106Hz)0.004～0.0004，脆化温度<-70℃，耐环境应力开裂(F50)>1000h。工业生产采用接枝共聚或无规共聚法。接枝共聚系在有机过氧化物存在下，聚乙烯与不饱和硅烷化合物经挤出机熔融混炼后，再在水作用下反应而成。无规共聚法系在高温、高压下，乙烯与乙烯基三甲氧基硅烷共聚，然后经水交联而成。主要用途有电线电缆包覆层、热收缩薄膜和套管、耐热管材、软管及工业输液管等。
CAS号：
性质：主链侧具有～Si—O～Si～交联网状结构的一种化学改性聚乙烯。改善了普通聚乙烯的耐热性、耐应力开裂性、耐蠕变性、耐冲击性、耐磨性、耐油性及低温特性。密度0.929g/cm3，凝胶率68%。拉伸强度38MPa，弯曲弹性模量1600MPa，悬臂梁缺口冲击强度110J/m，热变形温度(1.87MPa)101℃，体积电阻率>106Ω·cm，介质损耗因数(106Hz)0.004～0.0004，脆化温度<-70℃，耐环境应力开裂(F50)>1000h。工业生产采用接枝共聚或无规共聚法。接枝共聚系在有机过氧化物存在下，聚乙烯与不饱和硅烷化合物经挤出机熔融混炼后，再在水作用下反应而成。无规共聚法系在高温、高压下，乙烯与乙烯基三甲氧基硅烷共聚，然后经水交联而成。主要用途有电线电缆包覆层、热收缩薄膜和套管、耐热管材、软管及工业输液管等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。