1) pre-ceramic
![点击朗读](/dictall/images/read.gif)
有机硅先驱体
2) organic gel-polymer derived process
![点击朗读](/dictall/images/read.gif)
有机凝胶先驱体转化法
1.
CoNi alloy fine fibers had been successfully prepared by the organic gel-polymer derived process from the raw materials of critic acid and metal salts.
本文以柠檬酸和金属盐为原料,采用有机凝胶先驱体转化法成功制备了CoNi合金微细纤维。
2.
The spinel type MnFe2O4ferrite fibers are successfully prepared by the organic gel-polymer derived process from raw materials of metal salts and citric acid.
以柠檬酸和金属盐为原料,采用有机凝胶先驱体转化法成功制备出了纳米晶MnFe2O4铁氧体纤维。
3) Organic gel precursor transformation method
![点击朗读](/dictall/images/read.gif)
有机凝胶先驱体转化法
1.
The hollow M-type barium ferrite fibers were successfully prepared by the organic gel precursor transformation method from the raw materials of citric acid,lactic acid and their metal salts.
以柠檬酸、乳酸和金属硝酸盐为原料,采用有机凝胶先驱体转化法制备了中空M型(BaFe12O19)纤维。
4) polyearbosilane precurser
![点击朗读](/dictall/images/read.gif)
聚碳硅烷先驱体
5) inorganic precursors
![点击朗读](/dictall/images/read.gif)
无机盐先驱体
6) organic precursor
![点击朗读](/dictall/images/read.gif)
有机前驱体
1.
In this paper, Si3N4/SiC composite ceramics were prepared from two different raw materials with nano-SiC particles or organic precursor.
本研究通过采用纳米SiC粉体及有机前驱体两种途径,制备了Si3N4/SiC粒子(Si3N4/纳米SiC)复相陶瓷,研究了纳米SiC对SiN/SiC复相陶瓷性能及显微结构的影响,讨论了材料强化的机制与显微结构的关系。
2.
Two types of Si_3N_4/SiC nano-composites were prepared by means of organic precursor as raw material which was pyrolyzed and sintered under certain conditions.
本研究采用有机前驱体为主要原料,通过热解及烧结制备了两类Si_3N_4/SiC纳米复相陶瓷,研究了这些材料的显微结构特点,讨论了材料强化的机制及力学性能与显微结构的关系。
补充资料:先驱体法碳化硅纤维增强铝基复合材料
分子式:
CAS号:
性质:一种连续纤维增强金属基复合材料。有不含钛(商品名称Nicalon)和含钛(商品名称Tyranno)两种纺丝碳化硅纤维,与铝复合后一般含纤维40%(体积)左右,单向增强时纵向拉伸强度约为700~1000MPa,模量95~120GPa,密度约2.6g/cm3。主要的制造方法为各种液态渗透工艺。为了促进与铝的浸润,常用的制造方法是在超声波的作用下用连续铸造法先制成复合丝,然后再将复合丝热压成各种制品。也可以直接用压力铸造工艺制成各种零件。由于纺丝碳化硅纤维直径细,柔曲性好,此便于制造形状比较复杂的零件。
CAS号:
性质:一种连续纤维增强金属基复合材料。有不含钛(商品名称Nicalon)和含钛(商品名称Tyranno)两种纺丝碳化硅纤维,与铝复合后一般含纤维40%(体积)左右,单向增强时纵向拉伸强度约为700~1000MPa,模量95~120GPa,密度约2.6g/cm3。主要的制造方法为各种液态渗透工艺。为了促进与铝的浸润,常用的制造方法是在超声波的作用下用连续铸造法先制成复合丝,然后再将复合丝热压成各种制品。也可以直接用压力铸造工艺制成各种零件。由于纺丝碳化硅纤维直径细,柔曲性好,此便于制造形状比较复杂的零件。