1) impact single value
冲击功单值
1.
The original impact samples of E42 ship plate are analyzed, and the principal reason causing the impact single value fluctuating is found.
对E42船板原始冲击样进行物理分析,找出了引起冲击功单值波动的主要原因。
2) single strike work
单次冲击功
3) specific energy of shock
单位冲击功;冲击比功
4) Impact energy
冲击功
1.
Investigation on the correlation between fracture toughness and impact energy for middle strength steel;
中强钢断裂韧性和冲击功关系的研究
2.
Comparison of two kinds of models to predict the impact energy of the hot rolled Q235B in MaGang;
Q235B热轧板冲击功人工神经网络与线性回归预报模型的比较
3.
The results show that the impact energy increases and the yield strength decreases slowly with increasing the tempering temperature in the range of 200～600 ℃,and the impact energy increases and the strength decreases sharply when the tempering temperature is increased to above 600 ℃.
结果表明,25CrNi3MoV钢在200-600℃范围内回火时,随回火温度的升高,屈服强度缓慢下降、冲击吸收功缓慢增大;600℃以上回火时,强度急剧下降、冲击功迅速升高。
5) impact power
冲击功
1.
Influence of impact power on impact-corrosion resistance of low carbon high alloy steel;
冲击功对低碳高合金钢冲击腐蚀磨损性能的影响
2.
The property of impact-corrosion resistance of the low-carbon hi-alloyed steel has been tested in different impact power with the reconstructive impact-corrosion resistance machine.
利用改造的冲击腐蚀磨损机,测试了不同冲击功下低碳高合金钢的冲击腐蚀磨损性能。
3.
The results indicate that although the impact frequency of DTH hammer decreased somehow, the impact power increased.
结果冲击频率虽然有所下降 ,但其冲击功却有升高的趋势。
6) Impact work
冲击功
1.
The Un -qualified Reason Analysis of the Impact Work for Grade 35 Steel Forging Used for Pump Shaft;
35钢泵轴锻件冲击功不合格原因分析
2.
The linear relation between crushing specific work and the impact work and the temperature of ice.
研究冰在冲击载荷作用下发生破碎的状态，提出破碎比功的概念，分别建立了破碎比功与温度和冲击功的线性表达式。
3.
The results show that for the samples with remaining casting microstructure after normalizing,its tensile strength and elongation can be up to standard,and its fracture contraction rate reduces a little,but its impact work becomes lower than the samples with normal microstructure.
结果表明,正火不充分而残留铸态组织的铸钢试样,抗拉强度、伸长率均能达标,断面收缩率稍低,但冲击功却比正常组织试样低很多。
补充资料：邦德冲击破碎功指数
邦德冲击破碎功指数
Bond work index of impact crushibility
bongde ChongJJ Posujgong zh一shu邦德冲击破碎功指数(Bond work index ofimpaet erushibility)表征矿石可碎性的指标。该指数通过测定物料破碎时的能耗，反映物料可碎性。是美国邦德(F.C.Bond)于20世纪50年代提出的。 采用双摆锤冲击试验机，即低能冲击试验机(图l)进行测定。通常称为低能冲击破碎功指数。测定方法缨 图1低能冲击试验机是使被测物料两侧受到相同的冲击功。锤头质量m为13.6Ikg，摆锤长度L为711.Zmm，摆锤打击面为somm只somm。测定时取20块拉度为一75~+somm的物料，放置在砧座上，摆锤以5a的提升角度梯度逐渐升高，然后释放，直至击碎物料为止。用 Wi一2 .59KC/s，计算，式中Wic称为低能冲击破碎功指数;K为因次换算系数;C为单位试件厚度的冲击破碎功(称为可碎性系数)，c一KIK:(l一 cos争)/S，式中K:为仪器系数，K:为换算系数，小为摆锤最大摆角(物料破碎时的摆角)，s为试件厚度;S:为试料真密度。 1982年美国艾里斯一卡尔默斯(Allss一ehalmers)公司研制成功使用高能冲击试验机(图2)的高能冲击功指数测定技术。它与低能冲击试验不同之处是设置了冲击摆和回弹摆，用回弹摆吸收物料破碎后的多余能量，因此，一次高能冲击即可使物料破碎。高能冲击破碎功指数W，的计算公式为ha 图2高能冲击试验机 1一主冲击锤;2一主滑杆;3一回摆锤; 4一从动滑杆，5一刻度器;6一密封箱; 7一吊索;8一底架;9一上架 10 10 w:一W/(惹一惹’式中W为单位破碎能量;FS。为原料中80%通过的粒度;尸8。为产品中80%通过的粒度。被测定的原料粒度为20一somm。 低能冲击破碎功指数适用于计算物料粗碎的破碎能耗;高能冲击破碎功指数适用于计算物料中碎和细碎的能耗。 (王宏勋)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。