1) FRP grids
玻璃钢格栅
1.
The production process and mechanical properties of pultruled FRP grids are introduced in this paper.
本文介绍了一种拉挤模塑玻璃钢格栅的生产工艺及其力学性能。
2) windshield mold of toughened glass
玻璃钢化风栅
3) glass fiber grid
玻璃纤维格栅
1.
According to the construction practice,this paper sums up the construction technology of glass fiber grid in the practical pavement and some problems needing attention.
根据施工实践,总结出了玻璃纤维格栅在实际铺设中的施工工艺和应注意的问题。
2.
Based on the reconstruction of current rigid pavement overlay asphalt concrete cement, the paper studies the principle of restraining asphalt concrete pavement reflection crack and reducing rutting using glass fiber grid.
对在现有刚性路面加铺沥青混凝土层的改造中使用玻璃纤维格栅抑制路面反射裂和减少车辙的机理进行了初步探讨,并报告了深圳市景田东路路面改造的施工工艺和应用效果。
3.
The effects of glass fiber grid asphalt concrete and GoodRoad Ⅱ fiber asphalt concrete resisting reflection cracking caused by thermal stress of asphalt pavement on semirigid base were studied through fullscale test.
通过足尺疲劳试验,对玻璃纤维格栅沥青混凝土、GoodRoad 纤维增强沥青混凝土抑制半刚性基层沥青路面由于温度变化导致反射裂缝的作用效果进行了研究。
4) carbon/glass fiber gridgeo
碳/玻璃纤维格栅
5) GLASGRID
玻璃纤维格栅
1.
Now according to the climate character of the northwest area and the character of the pavement disease, we introduce the new pattern material ——GLASGRID to solve the reflection crack problem of the Northwest area.
根据西北地区气候特征以及路面病害特征，现引入新型材料——玻璃纤维格栅，以解决西北地区路面普遍存在的反射裂缝问题。
2.
According to the domestic and foreign researches, the new pattern material——GLASGRID is one effective method to solve the reflection crack problem.
根据国内外研究成果,采用铺设新型材料—玻璃纤维格栅的方法,是解决半刚性基层沥青路面反射裂缝问题的一个途径。
6) glassgrid
玻璃纤维土工格栅
1.
The fracture strength of three kinds of glassgrids under different loading rate were investigated.
对三种玻璃纤维土工格栅在不同的加载速率下的断裂强力进行了大量的试验研究,得到了断裂强力与加载速率的关系曲线。
2.
Based on static strength tests on two kinds of glassgrids,the fatigue experiment under constant amplitude loading of different stress level is carried out.
选取两种不同规格的玻璃纤维土工格栅,首先进行大量的静载强度试验,在此基础上,进行了不同应力水平下的恒幅疲劳试验,研究玻璃纤维土工格栅的P-S-N曲线、滞回曲线以及应变与循环次数的关系。
3.
To investigate the influence of hot-lay asphalt on mechanical property of glassgrid,three kinds of glassgrid set were selected and large numbers of experiments concerning temperature\'s influence on fracture strength and elongation rate were carried out at different temperatures.
为研究路面热铺沥青对玻璃纤维土工格栅力学性能的影响,选取了3种规格的玻璃纤维土工格栅,对不同温度作用的玻璃纤维格栅试样,就温度对其拉伸断裂强力和断裂伸长率2项力学性能的影响进行了大量的试验研究;并运用统计学中的柯尔莫哥洛夫检验法和格拉布斯准则对试验结果进行了分析及异常值剔除,得到其温度与拉伸力学性能关系曲线;在此基础上,运用标准不确定B类评定办法对试验结果进行了评定。
补充资料：玻璃纤维增强聚甲基丙烯酸甲酯透明玻璃钢
分子式：
CAS号：
性质： 玻璃纤维增强的有机玻璃。具有好的机械强度，冲击强度可比普通有机玻璃高5～10倍，半透明、耐光耐候性优良。制法与铸型本体聚合制有机玻璃相似，在模具中每铺一层玻璃纤维，浇一层甲基丙烯酸甲酯预聚浆料，使其充分浸润，最后密封后加热固化脱模。主要用作建筑材料，如遮阳板等。
CAS号：
性质： 玻璃纤维增强的有机玻璃。具有好的机械强度，冲击强度可比普通有机玻璃高5～10倍，半透明、耐光耐候性优良。制法与铸型本体聚合制有机玻璃相似，在模具中每铺一层玻璃纤维，浇一层甲基丙烯酸甲酯预聚浆料，使其充分浸润，最后密封后加热固化脱模。主要用作建筑材料，如遮阳板等。