1) reducing gases
还原气
1.
The reduction behavior of pellets reduction by different reducing gases were studied in the laboratory and pilot shaft of BL DR process.
用实验室还原装置和BL法试验竖炉研究了球团矿在不同还原气条件下的还原行为。
2) gas-based reduction
气基还原
1.
Dephosphorization of high-level phosphorus iron ore by gas-based reduction and melt separation
高磷铁矿气基还原冶炼低磷铁
2.
Influence of alkali salt on gas-based reduction of iron ore was studied.
通过气体催化还原氧化铁试验,研究了碱金属盐对气基还原铁氧化物反应的影响规律,对于同一种阳离子的盐催化活性规律为:氟化物>氯化物>碘化物>溴化物;硝酸盐>氢氧化物>碳酸盐>硫酸盐>磷酸盐。
3) reduction atmosphere
还原气氛
1.
The effects of reduction atmosphere on the structure of the Co-ZrO2 coprecipitation catalyst and its catalytic activity for Fischer-Tropsch synthesis were investigated by means of X-ray diffraction,transmission electron microscopy,scanning electron microscopy,and temperature-programmed reduction.
采用程序升温还原、氮吸附、原位X射线衍射、扫描电镜和透射电镜等方法研究了不同还原气氛对钴锆共沉淀催化剂结构的影响,并考察了催化剂上费托合成反应的性能。
2.
Influence of reduction atmosphere on property of 7%Pd/γ Al 2O 3 catalyst was studied.
本文研究了还原气氛对催化剂 7% Pd/γ- Al2 O3性能的影响。
3.
The PTCR thermistors which have a higher room temperature resistance than nominal ones, are treated under reduction atmosphere (lg{ p O 2 } Pa =-4.
对常温阻值大于标称阻值ＰＴＣＲ热敏电阻在还原气氛中（氧分压ｌｇ｛ｐＯ２｝Ｐａ＝－４。
4) reduction of oil-gas
油气还原
5) reducing atmosphere
还原气氛
1.
Effect of reducing atmosphere on composition and microstructure of cement clinker;
还原气氛对水泥熟料矿物组成及显微结构的影响
2.
After the Nd,Cr:GSGG crystal was annealed in reducing atmosphere,the absorption bands near 1μm almost disappear fully,which.
还原气氛(CO和H2)下退火后的吸收光谱中,在1μm处的吸收带基本消失,这对于提高激光效率是非常有利的。
3.
The influences of three factors,such as gas contents in reducing atmosphere,reducing temperature and reducing time,on the reducing degree of ware sintering were quantitatively investigated by the tube furnace.
利用管式炉定量研究了陶瓷烧成中还原气氛气体含量、还原温度和还原时间三者对日用瓷烧成还原程度的影响 。
6) Reducing Gas
还原煤气
1.
Expressions about reducing gas generating reaction by air-coal method were established.
建立了空气－煤炭法发生还原煤气的化学反应表达式。
补充资料：还原气氧化度
还原气氧化度
reducing gas oxidability
huanyuanq一yanghuadu还原气氧化度(redueing gas oxidability) 直接还原炼铁使用的还原气中氧化性成分(C 02+HZO)与非惰性气体成分(CO+H:+CO:+HZO)之比: CO，+H，O 甲一万石一下屯了下不下不不石下几了又100% C02+HZO+CO+HZ“”以/U式中叩为还原气氧化度，%;CO:，CO，H20，H:为还原气中各成分含量，环。当还原气中含有较多自由氧(02)，CH;或其他非惰性成分时，计算氧化度还应考虑这些成分的影响。 (赵庆杰)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。