1) BaO-SiO2-B2O3-TiO2 system glasses
BaO-SiO2-B2O3-TiO2系统玻璃
1.
The valency of titanium and the structure state of Ti3+ in BaO-SiO2-B2O3-TiO2 system glasses had been studied by using electron spin resonance (ESR) .
采用电子自旋共振(ESR)方法研究了钛在BaO-SiO2-B2O3-TiO2系统玻璃中的价态及Ti3+的结构状态。
2) BaO-La2O3-B2O3-SiO2 glass
BaO-La2O3-B2O3-SiO2玻璃
1.
Ce3+ and Tb3+ doped BaO-La2O3-B2O3-SiO2 glasses were prepared by conventional melt quenching technology.
采用传统熔体冷却技术制备Ce3+和Tb3+掺杂的BaO-La2O3-B2O3-SiO2玻璃,并测试样品的吸收光谱和荧光光谱。
3) TiO_2-BaO-SiO_2 system
TiO2-BaO-SiO2系统
1.
High refractive index glass beads for TiO_2-BaO-SiO_2 system were prepared.
以TiO2-BaO-SiO2系统为高折射率玻璃微珠的玻璃系统,采用X射线衍射、梯度炉、光学显微镜等测试手段探讨了玻璃微珠的析晶、成型方法和折射率的测定方法。
4) CaO-B2O3-SiO2 glass-ceramics
CaO-B2O3-SiO2系统微晶玻璃
5) SiO2-TiO2 glass
SiO2-TiO2系玻璃
1.
The degradation of chromate waste water by SiO2-TiO2 glass was introduced.
介绍了SiO2-TiO2系玻璃光催化降解含铬废水的实验。
6) CaO-B2O3-SiO2 glass
CaO-B2O3-SiO2玻璃
1.
CaO-B2O3-SiO2 glass powder was prepared by sol-gel process, TGA-DSC, XRD and SEM techniques were employed during the study.
采用sol-gel法制备了CaO-B2O3-SiO2玻璃粉体材料。
补充资料：CaO-TiO2-SiO2 ceramics
分子式：
CAS号：
性质：在CaO-TiO2-SiO2三元系统中以CaSiO3与TiO2或以CaTiSiO5与CaTiO3为基料的陶瓷材料。其结构特点是两种晶相共存，性能受晶相比例影响。配比可在一定范围内调节。主要原料为碳酸钙、二氧化钛、二氧化硅，加入少量改性添加剂，经配料、磨细、混合、成型、烧成等工序获得制品，也可先用碳酸钙和二氧化硅高温下合成硅酸钙，用碳酸钙、二氧化硅、二氧化钛高温下合成钛硅酸钙后再进行配料、烧成等，以确保两晶相共存。主要介电性能为：介电常数80～110，介质损耗角正切值(0.8～2.5)×10-4，介电常数温度系数(-450～+550)×10-6/℃。抗电温度(45～55)kV/mm，电阻率(1011～1012)Ω·cm。主要用作温度补偿型陶瓷电容器瓷料。
CAS号：
性质：在CaO-TiO2-SiO2三元系统中以CaSiO3与TiO2或以CaTiSiO5与CaTiO3为基料的陶瓷材料。其结构特点是两种晶相共存，性能受晶相比例影响。配比可在一定范围内调节。主要原料为碳酸钙、二氧化钛、二氧化硅，加入少量改性添加剂，经配料、磨细、混合、成型、烧成等工序获得制品，也可先用碳酸钙和二氧化硅高温下合成硅酸钙，用碳酸钙、二氧化硅、二氧化钛高温下合成钛硅酸钙后再进行配料、烧成等，以确保两晶相共存。主要介电性能为：介电常数80～110，介质损耗角正切值(0.8～2.5)×10-4，介电常数温度系数(-450～+550)×10-6/℃。抗电温度(45～55)kV/mm，电阻率(1011～1012)Ω·cm。主要用作温度补偿型陶瓷电容器瓷料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。