1) electrochemically anodize
有序多孔氧化铝模板
2) porous anodic aluminum oxide template
多孔氧化铝模板
1.
The α-iron nanowires array films were prepared by electrochemical deposition on the porous anodic aluminum oxide template with nanopores.
在具有纳米级孔洞的多孔氧化铝模板上, 用电沉积方法制备出α Fe纳米线有序阵列组装膜。
3) porous alumina template
多孔氧化铝模板
1.
Fabrication porous alumina template by anodization method;
阳极氧化法制备多孔氧化铝模板
2.
The surface morphology of porous alumina template was observed by emission-scanning tunneling microscopy(SEM) before and after the electrodeposition of Co nanowires.
采用扫描电子显微镜(SEM)对电沉积钴纳米线前后的多孔氧化铝模板的形貌进行表征,通过透射电子显微镜(TEM)观察钴纳米线的表面形貌。
4) porous alumina membrane
多孔氧化铝模板
1.
Electrochemical deposition of Co nanowire arrays in porous alumina membrane by alternating current method
多孔氧化铝模板中交流沉积钴纳米线阵列
5) ordered porous alumina
有序多孔氧化铝膜
6) porous anodic alumina
多孔阳极氧化铝模板
1.
Ni-Mo alloy nanowires were prepared using porous anodic alumina(PAA) as templates and were characterized by SEM and XPS.
使用多孔阳极氧化铝模板,电沉积制备了Ni-Mo合金纳米线。
补充资料：多晶氧化铝纤维
分子式：
CAS号：
性质：又称多晶氧化铝纤维。制法不同其Al2O3的结晶态和含量各异。直径10～20μm。密度2.7～4.2g/cm3。强度1.4～2.45GPa。模量190～385GPa。最高使用温度为1100～1400℃。制法：(1)前驱体法，将聚铝噁烷与硅酸酯载体溶于有机溶剂中干纺，在1000℃空气中烧成，得到含SiO2的γ-Al2O3纤维；更换原料和载体可得α-Al2O3-ZrO2纤维；(2)淤浆法，将α-Al2O3粉、Al(OH)2Cl·2H2O及少量MgCl2·6H2O所组成的淤浆干纺，在1000～1500℃烧成而得α-Al2O3纤维；(3)胶体法，在含HCOO-和CH3COO-离子的Al2O3溶胶中加入硅溶胶和硼酸，纺丝后烧成而得(9Al2O3·2B2O3+无定形SiO2)纤维。用作结构和功能复合材料增强剂，如电磁波屏蔽材料等。
CAS号：
性质：又称多晶氧化铝纤维。制法不同其Al2O3的结晶态和含量各异。直径10～20μm。密度2.7～4.2g/cm3。强度1.4～2.45GPa。模量190～385GPa。最高使用温度为1100～1400℃。制法：(1)前驱体法，将聚铝噁烷与硅酸酯载体溶于有机溶剂中干纺，在1000℃空气中烧成，得到含SiO2的γ-Al2O3纤维；更换原料和载体可得α-Al2O3-ZrO2纤维；(2)淤浆法，将α-Al2O3粉、Al(OH)2Cl·2H2O及少量MgCl2·6H2O所组成的淤浆干纺，在1000～1500℃烧成而得α-Al2O3纤维；(3)胶体法，在含HCOO-和CH3COO-离子的Al2O3溶胶中加入硅溶胶和硼酸，纺丝后烧成而得(9Al2O3·2B2O3+无定形SiO2)纤维。用作结构和功能复合材料增强剂，如电磁波屏蔽材料等。