1) Al-Zn-Cu ternary system
Al-Zn-Cu三元系
1.
The equilibrium relationship and composition of three solid solutions at the low Cu region in the Al-Zn-Cu ternary system has been investigated by means of diffusion couple-EPMA technique.
采用扩散偶-电子探针微区分析技术,对Al-Zn-Cu三元系相图的低Cu区三个固溶体相的相平衡关系及相平衡成分进行了研究。
2) Al-Zn-Cu ternary alloys
Al-Zn-Cu三元合金
3) Al-Zn-Cu system
Al-Zn-Cu系
1.
It was affirmed that the stable Al+Zn+T' three phase region exists, and the stable Al+Zn+CuZn4 three phase region dosen't in Al-Zn-Cu system at room temperature with experiment of SEM, EPMA and XRD.
利用扫描电镜、电子探针和X射线衍射实验确定了Al-Zn-Cu系在室温下存在稳态Al+Zn+T＇三相区,而不存在稳态的Al+Zn+CuZn4三相区。
4) Cu-Zn-In ternary system
Cu-Zn-In三元合金系
5) Al-Zn-Mg-Cu-Sc-Zr hexbasic system
Al-Zn-Mg-Cu-Sc-Zr六元系
1.
The current status of study of Al-Zn-Mg-Cu-Sc-Zr hexbasic system in the aluminum-rich region in recent years is reviewed.
总结了近年来Al-Zn-Mg-Cu-Sc-Zr六元系相图的发展情况,分析了Al-Zn-Mg-Cu-Sc-Zr六元系中富铝角存在的中间相Al3Sc、Al3Zr、Al3(Sc1-xZrx)、W相(ScCu6。
补充资料：Cu-Zn-Al shape memory alloy
分子式：
CAS号：
性质：一种含Zn l8％～37％(质量)、Al 2％～8％(质量)、余者为铜的具有形状记忆效应和伪弹性的合金。其Ms点在93～373K之间。其形状记忆应变约4％。该合金一般在大气或真空感应炉中熔炼，采用石墨或氧化铝坩埚。该合金易于冷热加工，如将其加热到(α+β)两相区，缓冷后得到两相组织，亦可进行冷拉。为了使合金形状记忆效应稳定，可以在423～473K油浴中进行等温淬火或一般淬火后在373K进行时效处理。该合金晶粒比较粗大，可加入微量元素V、B、Ti等使晶粒细化。
CAS号：
性质：一种含Zn l8％～37％(质量)、Al 2％～8％(质量)、余者为铜的具有形状记忆效应和伪弹性的合金。其Ms点在93～373K之间。其形状记忆应变约4％。该合金一般在大气或真空感应炉中熔炼，采用石墨或氧化铝坩埚。该合金易于冷热加工，如将其加热到(α+β)两相区，缓冷后得到两相组织，亦可进行冷拉。为了使合金形状记忆效应稳定，可以在423～473K油浴中进行等温淬火或一般淬火后在373K进行时效处理。该合金晶粒比较粗大，可加入微量元素V、B、Ti等使晶粒细化。