1) Cfibre/SiC/B4C
C纤维/SiC/B4C
2) C_ flake-SiC-B_4C
C鳞片-SiC-B4C
1.
FEM was used to study the ablation behavior of C_ flake -SiC-B_4C composite plate with different C_ flake contents and degrees of orderliness of C_ flake under aerodynamic heating conditions.
应用有限元法研究了在气动加热条件下不同含量和不同有序化程度C鳞片的C鳞片-SiC-B4C复合材料板的烧蚀行为·结果表明:环境介质温度、材料组分、相对密度以及不同有序化程度C鳞片对板状复合材料的瞬态温度场分布均有明显影响;C鳞片质量分数65%,基体中SiC和B4C的质量比约为5∶1,且C鳞片基本结构单元为有序排列时C鳞片生长连续并形成面积较大的碳层面,平行层状堆积成拱形结构时复合材料具有较强的抗氧化性,与实验结果一
3) C-B4C-SiC composite materials
C-B4C-SiC复合材料
4) silicon carbide fiber precursor
SiC-C纤维先驱体
5) C-SiC-B4C-TiB2 composite
C-SiC-B4C-TiB2复合材料
1.
C-SiC-B4C-TiB2 composites were prepared with raw materials such as flake graphite Cfg,SiC,B4C and TiO2 by in situ synthesis and hot pressed.
以磷片石墨Cfg,SiC,B4C和TiO2为原料,热压合成C-SiC-B4C-TiB2复合材料,研究不同Cfg含量和热压温度对复合材料显微组织和力学性能的影响规律。
6) SiC B 4C Zr C/C composites
SiC-B4C-ZrC/C复合材料