1) cyanate ester of novolac
酚醛三嗪树脂
1.
Two kinds of cyanate ester of novolac are synthesized with self-made phenolic resin varnish and high purity novolac.
分别以酚醛清漆、高纯酚醛为改性基体制备了酚醛三嗪树脂,并运用热失重分析(TGA)研究了树脂的耐热性及残炭率。
2) phenolic-triazine
酚-三嗪树脂
3) Phenolic triazine resin
酚三嗪树脂
4) phenolic resin with three components
三组份酚醛树脂
1.
It is suggested in this paper that phenolic resin with three components and hybrid fiber were used to prepare clutch friction materials by cold-press process.
三组份酚醛树脂为硼改性腰果壳油液体树脂、三聚氰胺改性酚醛液体树脂和芳烷基改性酚醛固体树脂。
5) phenolic resin
酚醛树脂
1.
Preparation of porous carbon foams using phenolic resin as precursor;
酚醛树脂为前驱体制备多孔碳泡沫材料
2.
Synthesis and characterize a new type highly-heat-resistant phenolic resin;
一种高耐热酚醛树脂的合成及表征
3.
Synthesis and properties of boron-and-silicon-containing phenolic resin;
硼硅双改性酚醛树脂的合成与性能
6) PF resin
酚醛树脂
1.
The development of wood PF resin adhesive;
木材工业用酚醛树脂胶粘剂的现状及研究进展
2.
Special PF Resin for Light-alloy Coated Sand;
轻合金覆膜砂专用酚醛树脂的开发研究
3.
Using pyrolytic tar from larch bark as partial substitute for phenol in proportions of 0%, 20%, 40%, 60% , four types of PF resins were prepared and applied in hot-pressing three- layer poplar plywood by orthogonal test methods with different levels of press pressure, press time, and and resin content.
以落叶松树皮热解油按比例0%、20%、40%、60%代替苯酚制备的4种酚醛树脂胶黏剂和人工林杨木单板为原料,采用正交实验设计方法,选择不同的热压压力、热压时间和涂胶量进行了3层胶合板压制试验。
补充资料：三嗪树脂
分子式：
CAS号：
性质：又称氰酸酯树脂（cyanate resin）。一种含均三嗪环的热固性树脂。R1、R2是芳香基团，R′是亲电子基团，为杂环状树脂。无色液体，真空脱溶剂后则成为B阶预聚物。可溶于甲醇、乙醇、丙酮和甲乙酮。由仲双氰胺和伯双氰胺和在甲醇（或乙醇、丙酮）等溶剂中进行溶液聚合制得预聚物。可由酚型双氰酸酯或多氰酸酯三聚化形成均三嗪环和交联结构。预聚物树脂具有可熔可溶性，溶于丙酮等通用溶剂，环化反应主要在成型加工过程中进行，适用作耐热性均大大高于环氧树脂基复合材料。用玻璃布、石棉、纸和石墨纤维增强的层合材料可做工程结构件，也可做模塑料、浸渍漆或胶黏剂。