1) ammonium polyphosphate (APP) form II
结晶Ⅱ-型聚磷酸铵
2) Ⅱ-type ammonium polyphosphate
Ⅱ型聚磷酸铵
1.
The methods of horizontal burning,the amount of carbon residue and so on were used to evaluated properties of plastic-wood composites (WPC) flame retardanted byⅡ-type ammonium polyphosphate.
以Ⅱ型聚磷酸铵为阻燃剂制备了阻燃塑木复合材料并通过水平燃烧、成炭量等评价了材料的综合性能。
4) ammonium polyphosphate
聚磷酸铵
1.
Study on the role of ammonia in preparation of crystal formⅡammonium polyphosphate;
结晶Ⅱ型聚磷酸铵制备过程中氨的作用研究
2.
Limitation of test method of average degree of polymerization of ammonium polyphosphate by end grouptitration;
端基滴定法测试聚磷酸铵平均聚合度的局限性
3.
Preparation of siloxane-enwrapped ammonium polyphosphate and its application in coating agents;
硅氧烷包覆聚磷酸铵协同阻燃剂的制备及在涂层剂中的应用
5) APP
聚磷酸铵
1.
Effect of flame retardant APP on properties of dealcoholized RTV-1 silicone rubber;
阻燃剂聚磷酸铵对脱醇型RTV-1硅橡胶性能的影响
2.
STUDY ON THE ABLATION PROPERTY OF INSULATOR MATERIAL ENHANCED BY LDA/APP;
用聚磷酸铵和联二脲来提高绝热层材料耐烧蚀性能的研究
3.
The Fire Retardancy of Wood Flour/PS Composites Treated with APP-Starch;
聚磷酸铵-淀粉对木粉/聚苯乙烯复合材料的阻燃作用
6) ammonium polyphosphate
多聚磷酸铵
1.
Five triazine derivatives were synthesized as charring agent and respectively incorporated with ammonium polyphosphate(APP) to prepare intumescent flame retardants(IFR).
设计并合成了５种不同分子结构的三嗪衍生物，将它们分别与多聚磷酸铵复配组成膨胀型阻燃剂（ＩＦＲ）体系。
2.
As a result of LOI, appreciable distinction could be revealed between flame retardant properties of PE/GIG, among which PE/GIC intercalated by ammonium polyphosphate possessed the .
研究表明,不同含磷化合物插层GIC阻燃聚乙烯的氧指数有显著差别,其中以多聚磷酸铵-GIC的阻燃效果较好,氧指数较高。
补充资料：聚磷酸铵
聚磷酸铵分子通式为(NH3)n+2PnO3n+1。白色粉末，密度1．74；在强酸溶液中断链生成磷酸铵。近于中性，分散性好，与其他物质不起反应。热稳定性好，分解温度不低于250℃。低毒。
用作添加型阻燃剂。受热分解时生成氨及非常稳定的聚合磷酸，可成为高分子聚合物的保护层而将氧隔绝。也可与其他阻燃剂复合使用。
用作添加型阻燃剂。受热分解时生成氨及非常稳定的聚合磷酸，可成为高分子聚合物的保护层而将氧隔绝。也可与其他阻燃剂复合使用。