1) Ni-Fe-Ga-Co magnetic shape memory alloys
Ni-Fe-Ga-Co磁性形状记忆合金
1.
The microstructure, thermally-induced martensitic transformation, magnetic properties and mechanical behavior of Ni-Fe-Ga-Co magnetic shape memory alloys have been studied by means of optical microscope, TEM, XRD and DSC as well as TG and tensile test at room temperature.
本文采用光学显微镜、透射电子显微镜、X射线衍射分析、差示扫描量热仪以及磁场下的热重分析和室温拉伸试验等,研究了Ni-Fe-Ga-Co磁性形状记忆合金的组织结构、马氏体相变、磁性能以及力学行为,揭示了合金成分和热处理工艺对γ相析出的影响规律,阐明了γ相增韧的微观机制。
2) Ni-Mn-Ga MSM alloy
Ni-Mn-Ga磁性记忆合金
3) Ni-Ga-Fe-Co alloy
Ni-Ga-Fe-Co合金
4) Ni-Fe-Ga-Co alloy
Ni-Fe-Ga-Co合金
5) Fe-Mn-Si-Cr-Ni shape memory alloy
Fe-Mn-Si-Cr-Ni形状记忆合金
1.
Microstructure of the weld joints in a tungsten-insert gas(TIG) welded Fe-Mn-Si-Cr-Ni shape memory alloy was investigated by using scanning electron microscope and X-ray diffraction,and shape memory effect of the weld joints was examined by bending tests.
利用扫描电镜、X射线衍射仪对Fe-Mn-Si-Cr-Ni形状记忆合金钨极氩弧焊(TIG焊)接头组织进行分析,并利于弯曲变形法考察了焊接接头的形状记忆效应。
6) Co-Ni-Ga alloy
Co-Ni-Ga合金
补充资料：高温形状记忆合金
分子式：
CAS号：
性质：一般指高于普通形状记忆合金工作温度上限的形状记忆合金。高温形状记忆合金是在TiNi中加入Au，Pt或Pd取代Ni，用以提高相变点。其中有实用价值的是TiNi-Pd系。它有较高形状记忆应变(5％～6％)。随钯含量增加，形状恢复温度As最高可达到560℃。TiNi-Pd高温形状记忆合金的形状记忆效应机理与TiNi记忆合金类似，为热弹性马氏体相变时，相界/畴界作可逆运动，Ti50Nil3Pd37是TiNi-Pd系高温记忆合金的一种，形状恢复温度As为347℃，相变热滞为8℃，形状记忆应变为6％，室温和350℃断裂强度分别为1112MPa和918MPa。
CAS号：
性质：一般指高于普通形状记忆合金工作温度上限的形状记忆合金。高温形状记忆合金是在TiNi中加入Au，Pt或Pd取代Ni，用以提高相变点。其中有实用价值的是TiNi-Pd系。它有较高形状记忆应变(5％～6％)。随钯含量增加，形状恢复温度As最高可达到560℃。TiNi-Pd高温形状记忆合金的形状记忆效应机理与TiNi记忆合金类似，为热弹性马氏体相变时，相界/畴界作可逆运动，Ti50Nil3Pd37是TiNi-Pd系高温记忆合金的一种，形状恢复温度As为347℃，相变热滞为8℃，形状记忆应变为6％，室温和350℃断裂强度分别为1112MPa和918MPa。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条