1) reduction condition
还原条件
1.
The silica-supported nickel phosphide,Ni2P/SiO2,was prepared by the temperature-programmed reduction method,and the influence of reduction conditions(H2 flow rate,reduction temperature,and time)on the textural properties of the catalyst was investigated.
采用程序升温还原方法制备了Ni2P/SiO2催化剂,考察了还原条件对催化剂结构及其催化氯苯加氢脱氯反应性能的影响。
2) reducing condition
还原性条件
1.
The structure development of coal chars under high temperature reducing conditions was studied.
研究了在高温还原性条件下煤焦的孔隙结构的变化规律。
3) The condition of Fe~(3+) reduction
铁还原条件
4) reducing condensers
还原条件<冶>
5) sulfate-reducing conditions
硫酸盐还原条件
1.
The characteristics of aniline degradation during the riverbank filtration process under sulfate-reducing conditions were researched.
采集渭河河床沉积物及沿岸地下水含水层介质,装置土柱进行动态实验,研究了硫酸盐还原条件下,苯胺在河岸渗滤过程中的转化特征。
6) optimum reduction condition
最佳还原条件
1.
5 g,the optimum reduction condition for the preparation of oxygen-deficient nickel ferrite,NiFe2O4-δ,reduced by H2 was as follows: reduction temperature was 320 ℃,H2 flow rate was 40 mL/min and reduction time was 3 h.
5g时,利用H2还原制备氧缺位NiFe2O4-δ的最佳还原条件为还原温度320℃、氢气流量40mL/min、还原时间3h。
补充资料：蓝钨氢还原(见仲钨酸铵氢还原)
蓝钨氢还原(见仲钨酸铵氢还原)
hydrogen reduction of blue tung sten compound
Ianwu qing huanyuan蓝钨氮还原(hydrogen reduetion of bluetungsten compound)见仲钨酸按氮还原。