1) Cu-Ag middle alloy
铜-银中间合金
1.
The result of the test indicates that the mass fraction of Ag in Cu-Ag middle alloy is two to ten percent, the relative standard deviation of the determination is 0.
平行测定结果表明,铜-银中间合金中银的质量分数在2%～10%之间,银含量测定的相对标准偏差为0。
2) copper master alloy
高铜合金;铜基中间合金
3) Ag-Cu alloy
银铜合金
1.
This paper summarizes the usual technology methods of producing Ag-Cu alloy contact wire used for electrical railway,explains the necessity to develop new technology,develops a new method of producing Ag-Cu alloy contact wire,that is continuous extrusion method.
概述了电气化铁路银铜合金接触线的常用工艺方法,说明了研究新的接触线制造工艺的必要性,并提出了新的银铜合金接触线制造方法———连续挤压法。
2.
The technological specificity of the continuous extrusion forming for Ag-Cu alloy and the effects of several process parameters, such as extrusion temperature, extrusion wheel rate, extrusion ratio and flash gap, on the process were analyzed and discussed.
分析讨论了银铜合金连续挤压工艺特点及挤压温度、挤压轮转速、挤压比、溢料间隙对连续挤压制品质量的影响。
4) Cu-Ag alloy
铜银合金
1.
Cu-Ag alloy is used as the contact wire of electrization railway, its strength and friction-wear properties have a important influence on its application.
铜银合金作为电气化铁路的接触线材料,其强度和摩擦磨损性能对其使用有很大影响。
5) gold-silver-copper alloys
金银铜合金
6) tumbago
[tʌm'beiɡəu]
铜、金、银合金
补充资料：钯银铜合金
分子式：
CAS号：
性质：是钯含银和铜的三元合金。在富钯区合金为单相固溶体，随温度升高单相区扩大。铜能提高合金的强度并可以缩小合金的凝固区间。在高温下大部分合金都为单相固溶体，在低温下出现PdCu和PdCu3为基的有序相。有PdAgCu36-4、PdAgCu65-5和PdAgCu65-20等合金。用真空中频炉充氩保护熔炼，多次冷凝除气，淬火态合金易加工成材。用作电位器绕组材料、滑动接点材料，含10%～25%Pd的合金具有良好的流动性和润滑性，可做高温无焊剂的钎料。饰品材料。
CAS号：
性质：是钯含银和铜的三元合金。在富钯区合金为单相固溶体，随温度升高单相区扩大。铜能提高合金的强度并可以缩小合金的凝固区间。在高温下大部分合金都为单相固溶体，在低温下出现PdCu和PdCu3为基的有序相。有PdAgCu36-4、PdAgCu65-5和PdAgCu65-20等合金。用真空中频炉充氩保护熔炼，多次冷凝除气，淬火态合金易加工成材。用作电位器绕组材料、滑动接点材料，含10%～25%Pd的合金具有良好的流动性和润滑性，可做高温无焊剂的钎料。饰品材料。