1) intercrystalline precipitation
沿晶界析出
2) Intergranular precipitation
沿晶析出
3) Grain Boundary Precipitates
晶界析出相
1.
With methods of grain boundary extraction carbon replica,the variation of grain boundary precipitates with process- ing parameters and chemical compositions of three superalloys strengthened to different extent was studied.
用晶界萃取碳复型技术研究了三种不同强化程度高温合金晶界析出相随工艺因素和成分的变化规律,探讨了晶粒尺寸、晶界析出相与冲击韧性的关系。
4) grain boundary precipitate
晶界析出物
5) precipitate free zone
晶界无析出带
1.
TEM and EDS analyses show that the precipitate free zones.
显微组织分析及微区成分分析表明,较短时间的回归处理所引起的晶界无析出带经过再时效后变窄甚至消失。
2.
TEM observation showed that the grain boundary precipitate free zones (PFZ) narrowed with accelerated quenching rate, yet gradually widened with the nucleation and growth of the grain boundary precipitated phase during aging.
结果表明，晶界无析出带（ＰＦＺ）随淬火速度的提高而变窄；而时效过程中，随着晶界沉淀相的形核和长大，ＰＦＺ逐渐宽化。
6) precipitate free zones
晶界无析出带(PFZ)
补充资料：沿晶断裂
沿晶断裂
intercrystalline fracture
yanjing duanlie沿晶断裂(intererystalline fraeture)金鼠材料中的裂纹沿晶界扩展而产生的一种断裂。当沿晶断裂断口形貌呈粒状时又称晶间颗粒断裂。多数情兄下沿晶断裂属于脆性断裂，但也可能出现韧性断裂，女口高温蠕变断裂。产生沿晶断裂一般有3种原因:(l)晶界上有脆性沉淀相。如果脆性相在晶界面上覆盖得不连续，例如AIN粒子在钢的晶界面上的分布，将产主微孔聚合型沿晶断裂;如果晶界上的脆性沉淀相是奎续分布的，例如奥氏体Ni一Cr钢中形成的连续碳化勿网状，则将产生脆性薄层分裂型断裂。(2)晶界有使其弱化的夹杂物。如钢中晶界上存在P、S、As、Sb、Sn等元素。(3)环境因素与晶界相互作用造成的晶界弱化或脆化，例如高温蠕变条件下的晶界弱化，应力腐蚀条件下晶界易于优先腐蚀等，均促使沿晶断裂产生。 沿晶脆性断裂断口宏观形貌一般有两类:(l)晶位特别粗大时形成石块或冰糖状断口;(2)晶粒较细时形成结晶状断口。沿晶断裂的结晶状断口比解理断裂均结晶状断口反光能力稍差，颜色黯淡。将金属进行是纯、净化晶界、防止杂质原子在晶界偏聚或脱溶(见目溶处理)、防止第二相在晶界上析出、改善环境因素等，均可减少金属发生沿晶脆性断裂的倾向。 (杨觉先)