1) lifting temperature reduction method under load
荷重升温还原法
1.
Experiment on checked reducing—powdered property of high Titanium sinter with lifting temperature reduction method under load was done.
进行了荷重升温还原法检验高钛型烧结矿的还原粉化性实验 ,分析研究了高钛型烧结矿在高炉内中低温区的还原粉化行为以及 F e O含量对烧结矿还原粉化和透气性的影响 ,结果表明 ,提高高钛型烧结矿的 Fe O含量可改善其还原粉化性能 ,Fe O含量以 8%～ 10 %为
2) hyperthermic reduction
升温还原方法
3) heating/reducing
升温还原
1.
introduction was made for structure features of 2400mm inner-heat change type of low pressure radial flow ammonia converter internals in china and for process flow of ammonia synthesis system,the filling of catalyst,heating/reducing schemes and operating data were discussed for internals of ammonia converter,the operating effect of actual production was summarized.
介绍了国内2400mm内换热式低压径向氨合成塔内件的结构特点及合成系统工艺流程;论述了氨合成塔内件触媒的装填、升温还原方案和操作数据,总结了实际生产运行效果。
2.
the extracted gas was separated from third stage outlet of shifting,the process flow sheet and process features were introduced;the improvement for heating/reducing process and production operation w.
介绍了工艺流程和工艺特点;论述了新增的2套甲醇合成装置催化剂的升温还原过程和生产操作的改进;分析了影响催化剂使用寿命的因素;提出了延长甲醇催化剂使用寿命的生产操作控制方法;总结了改进后装置生产运行效果。
4) heating reduction
升温还原
1.
Heating reduction and application of NC74-1 ammonia synthesis catalyst;
NC74-1型氨合成催化剂的升温还原及应用
2.
Filling data,distribution of temperature measuring points and heating reduction scheme were introduced for NC501 type methanol catalyst,the reduction process and production operation situation for this catalyst were discussed,through the comparison of production operation data for two furnaces of catalyst i.
介绍了NC501型甲醇催化剂的装填数据、测温点分布和升温还原方案,论述了该催化剂的还原过程和生产运行情况,通过NC501型和C207型两炉催化剂生产运行数据的对比,对NC501型催化剂的使用效果进行了总结。
5) temperature-increasing reduction
升温还原
1.
This article introduces the layer-by-layer temperature-increasing reduction of A203 Low-temperature ammonia Synthesis catalyst.
介绍A203型低温氨合成催化剂的分层升温还原,对它的装填及升温还原的控制进行总结。
6) reduction
[英][rɪ'dʌkʃn] [美][rɪ'dʌkʃən]
升温还原
1.
In this article,the author briefly introduced the application condition of C307 catalyst for LP methanol synthesis in our plant,primary analyzed the influence of reduction status of catalyst,ingredient of inlet syngas,H/C ratio,space-velocity to methanol synthesis,put forward the suitable measures for catalyst protection and operation method.
介绍了C307型低压甲醇催化剂在我厂的实际运行情况,初步探讨了催化剂升温还原状况、入塔气气体成分、氢碳比、空速等因素对甲醇合成反应的影响,并提出了行之有效的催化剂保护措施和合理的生产运行方式。
2.
Loading and reduction of catalyst A202Q, A110-5Q is described.
简述A2 0 2Q、A110 - 5Q催化剂的装填及升温还原过程 ,并对该过程中出现的问题及教训加以总结。
补充资料：荷重还原透气性
荷重还原透气性
permeability of iron ore bed during reduction under load
的阻力增加，从而影响料柱透气性和高炉顺行。矿石料层在高炉内加热还原状态下的透气性不同于它在冷态下的透气性，前者与矿石的矿物组成、化学成分和其它物理化学性质有关。因此，荷重还原透气性是评价不同矿石的高温冶金性能的重要指标之一。 6毓、 _11 llL竺云三兰三一10 臀9 高温还原荷重条件下料层的透气性测定装置 1一压差计;2一秤;3一加压气缸;4一料层高度标尺;5一活塞杆; 6一气体出口;7一热电偶;8一活塞气缸;9一氧化铝球， 10一煤气入口;n一带孔压板;12一试样 测试装置和方法2。世纪60年代德国的伯格哈特(0.Burghardt)和格列勃(K.Grebe)提出一种测定矿石在荷重还原条件下料层透气性的方法和装置(见图)。他们将软化性、还原性和透气性的测定结合起来，对于综合评价矿石的冶炼性能很有意义。测试的方法是在电炉中放置一根内径为125mm的双壁耐热金属反应管，管内放置试样，试样支托着压杆和对压杆施加荷重的压缩空气气缸。金属反应管等悬吊在电子称上，通过A/D转换器和差压变送器将电子秤读数(g)和压差(Pa)纪录在纪录仪上。试样的软化收缩率用位移传感器显示。还原气体经双壁金属管的夹缝进行预热，试样的温度由设置在试样层上下约Zomm处的Cr一Al热电偶进行测量。试样的压差在内管试样的底和顶部之间测量。试验时，取12009粒度为10~12.smm的矿石试样，置于反应管内开有若干小孔的算板上。试样上下各放置两层A1203球。试样首先在SOL/min的N:气流中加热，当达到1050℃时，保持恒温并切换为83.3L/min的还原气，成分为N:60%士0.5%和C040%士0.5%。在试验中，试样每失重509就测定一次试样的收缩率。当还原度达到80%或还原时间达15omin时，切断还原气停止试验。将装有试样的反应管从炉内取出并在N:气中冷却，然后从中取出试样进行分析。伯格哈特装置测得的荷重还原透气性，可以反应在较高温度下矿石的还原性、膨胀性、软化性和热裂等因素对料层透气性的综合影响，但不能反映低温.还原粉化和高温熔化滴落的影响。 评价指标用伯格哈特装置测定矿石荷重还原透气性的评价指标有3个:(1)还原度为80%(或还原15omin)时的气流压差。这一压差不包括还原开始前的原始压差，压差愈高表明矿石高温还原后的粉化愈严重、软熔愈早，收缩愈大，透气性愈差;利用压差低的矿石有利于改善料柱透气性和高炉冶炼。(2)还原度为80%时的料层收缩率。(3)还原度40%时的还原速率(%/min)。 影响因素荷重还原透气性主要同矿石在加热还原过程中的膨胀、开裂、粉化和软化有关。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。